Biodegradation of Low Density Polyethylene by Selected Bacillus sp.
Summary
Researchers found that certain Bacillus bacteria can degrade low-density polyethylene (LDPE) plastic, breaking it down at a modest 1.5% over 60 days. While the rate is slow, this points to a potential biological pathway for plastic degradation that could be developed further.
The necessity of environment friendly disposal policies designed for the biodegradation of synthetic plastics is tremendously crucial and need attention in the present scenario, considering the hazardous impact of widely used packaging material such as Low Density Polyethylene (LDPE) on the environment. Our study aims to explore the degradation of LDPE by three strains of Bacillus sp. i.e ISJ51, ISJ55 and ISJ57. The magnitude of biodegradation was evaluated by several techniques comprising weight loss of the polyethylene sample, reduction in bacterial hydrophobicity and estimation of biomass attached to the polyethylene film. The maximum biodegradation i.e., 1.5%, as well as protein content (0.75 μg/cm2) of bacterial biofilm adhered on LDPE was observed in Bacillus sp. strain ISJ55 after 60 days of treatment. ISJ55 also demonstrated more hydrophobicity in comparison to ISJ51 and ISJ57, since, a 20.3% reduction in culture turbidity was specifying better attraction towards hydrophobic substances. SEM analysis revealed that ISJ55 exhibited morphological changes in polyethylene surface while FTIR images showed functional changes after an incubation of 60 days. The establishment of biofilms on polyethylene surface and adhesion capabilities of bacteria are deliberated as the first step in the process of biodegradation. Therefore these results show that the isolate ISJ55 can colonize, modify and utilize LDPE as a sole carbon source, signifying the potential of Bacillus sp. to degrade LDPE film. This manuscript also paves the way for future studies on biodegradation to resolve the universal issue.
Sign in to start a discussion.
More Papers Like This
Degradation of low density polyethylene by Bacillus species
Researchers tested the ability of two common Bacillus bacteria species to degrade low-density polyethylene and observed weight losses of about 3.5 and 2.8 percent over 30 days. Surface analysis revealed cracks, pits, and chemical oxidation on the plastic sheets exposed to the bacteria. The study suggests that these widely available microorganisms could potentially be developed as biological agents for polyethylene degradation, though the underlying enzymatic mechanisms require further investigation.
Biodegradation of LDPE plastic by local strain of Bacillus sp. isolated from dump soil of Pekanbaru, Indonesia
Scientists isolated a local strain of Bacillus bacteria from landfill soil in Indonesia and tested its ability to break down low-density polyethylene (LDPE) plastic. The bacteria showed measurable ability to degrade LDPE, reducing plastic weight over time. This research supports the potential for using locally sourced soil bacteria in plastic biodegradation efforts.
Microbial degradation of virgin polyethylene by bacteria isolated from a landfill site
Researchers isolated bacteria from landfill sites that had been exposed to plastic waste for up to 17 years and tested their ability to break down high-density polyethylene (HDPE), a common plastic used in packaging. The bacterium Bacillus cereus achieved the highest degradation at only 1.78% weight loss, confirming that plastic biodegradation in landfills is an extremely slow process.
Biodegradation of Low Density Polyethylene (LDPE) using marine bacteria isolated from tropical beaches of megacity Mumbai
Marine bacteria isolated from plastic debris buried in beach sediments at seven Mumbai beaches were able to colonize and partially degrade low-density polyethylene (LDPE) plastic. Identifying bacteria naturally adapted to plastic-rich marine environments is a step toward developing biological tools for plastic degradation, though the process is currently far too slow to address the scale of ocean plastic pollution without significant enhancement.
Exploitation of bacterial strains for microplastics (LDPE) biodegradation
Researchers tested five bacterial strains for their ability to biodegrade low-density polyethylene microplastics over four months. Pseudomonas aeruginosa showed the most significant degradation with an 18.2% weight loss, followed by Bacillus subtilis at 16.1%. The study demonstrates that naturally occurring soil bacteria can break down polyethylene microplastics, suggesting a potential biological approach to addressing plastic waste pollution.