Ultraviolet-C and vacuum ultraviolet inducing surface degradation of microplastics
Summary
Researchers studied how UV-C and vacuum ultraviolet irradiation affect the surfaces of four common microplastic types during water disinfection. They found that standard UV doses used in wastewater treatment had little effect, but higher doses caused significant surface cracking, chemical bond breakdown, and changes in hydrophobicity. The study suggests that UV disinfection in wastewater plants can alter microplastic surface properties, which may affect how these particles interact with pollutants and organisms downstream.
Wastewater treatment plants (WWTPs) are considerable microplastics (MPs) contributors to environmental waters. Knowledge about the MPs degradation process under ultraviolet irradiation was crucial to understanding the fate of MPs during and after water disinfection. In this study, surface alternations of polystyrene (PS), polyethylene (PE), polyvinylchloride (PVC) and polyethylene terephthalate (PET) under 254 nm (UV-C) and 185/254 nm (vacuum ultraviolet, VUV) irradiation were estimated. One-way treatment of MPs by UV or VUV with the recommended dose for WWTPs (USEPA, ~180 mJ cm) had little effect. In contrast, excessive exposure under twenty-times doses irradiation (3600 mJ cm) resulted in significant alternations on surface morphology, chemical feature and hydrophobicity. Noticeably morphology alterations, including cracks, wrinkles and protuberances, were observed for PS, PVC and PET, while PE was relatively resistant. Fourier transform infrared spectroscopy and X-ray photoelectron spectroscopy revealed that UV irradiation induced cleavage of chemical bonds. Besides, simultaneous radical oxidation was predominant during VUV treatment, which contributed to the increasing generation of oxygen bonds, such as CO and CO, on all MPs surfaces. Drastic decreases of contact angle (> 20°) were observed for PS, PVC and PET even after 180 mJ cm UV irradiation, indicating the UV disinfection in WWTPs can easily change their surface hydrophobicity. All these alternations weakened the adsorption capacity of non-polar benzene and polar ciprofloxacin on MPs. Generally, regular dose UV and VUV irradiation in water treatment disinfection can only induce slight effects on MPs surface characteristics and adsorption performance, while extreme dose irradiation can induce a potential reducing risk of organic contaminants migration along with MPs.
Sign in to start a discussion.
More Papers Like This
Transformation of microplastics during UV-LED based water disinfection: Mechanistic insights and environmental implications
Researchers investigated how UV-based water disinfection treatments transform the physical and chemical properties of common microplastics like polystyrene, polyethylene, and PVC. They found that treatment created surface cracks, reduced water repellency, and generated various breakdown compounds, some of which showed toxicity to aquatic organisms. The study highlights that while UV disinfection effectively treats pathogens, it may inadvertently create new environmental risks by altering microplastics in the water supply.
Investigation of Surface Alteration of Microplastics by Using UV Irradiation
UV radiation causes polystyrene and other plastic microparticles to undergo photooxidative degradation, changing their surface chemistry and potentially making them more likely to adsorb or release chemical pollutants. Understanding these weathering processes is important for predicting the environmental behavior and toxicity of microplastics.
Modifications of ultraviolet irradiation and chlorination on microplastics: Effect of sterilization pattern
Researchers found that both UV irradiation and chlorination used in drinking water treatment alter the surface properties, size distribution, and chemical composition of microplastics, with combined treatments producing greater modifications and potentially increasing the release of plastic additives and adsorbed contaminants.
The effects of uv-radiation on the removal of microplastics in water using agglomeration-micro-flotation
Researchers investigated how UV radiation affects the surface wettability of six types of microplastics and its influence on removal efficiency via agglomeration-micro-flotation in water. UV treatment altered surface properties of the microplastics, and results showed that the modified wettability affected flotation performance, offering insights into using UV pre-treatment to enhance microplastic removal in water treatment systems.
Comparison of surficial modification of micro-sized polyethylenein between by UV/O3 and UVO submerged system
Researchers compared ozone and UV oxidation methods for chemically modifying the surface of polyethylene microplastics in water, finding that different treatment combinations create distinct surface changes. Understanding how weathering alters microplastic surfaces is important for predicting their environmental behavior and toxicity.