The characteristic change of plastic film from common used packing bags under UV photodegradation
AI summary Read the abstract
Researchers studied how UV light degrades plastic packaging films over time, finding that photodegradation causes surface cracking and chemical changes that progressively break plastic into smaller fragments, including microplastics. The findings help explain how discarded plastic packaging contributes to microplastic accumulation in the marine environment.
Since its invention, plastic has brought great changes to our daily life. It is considered as one of the most basic materials for the development of modern society. Most of the plastic produced are used for packaging and disposable products. Due to the high disposable rate and mismanagement, a large amount of plastic debris enters the marine environment. Potentially lasting several hundred years in the environment, the large plastic debris can be continuously broken into microplastics which are smaller than 5 mm under the action of ultraviolet light, heat, wind, tide, wave and bacteria etc. Therefore, the amount of microplastics will keep rising in the ocean. Microplastics is considered as a new emerging pollutant and has become a global concern. Understanding the degradation process of plastic in the environment is important for evaluating the contribution of plastic debris as one microplastics source. In this work, polyethylene film from 6 kinds of packaging bags commonly used in our daily life, i.e., food packing bag, garbage bag, thick film, and express packing bag, were selected to carry out photodegradation experiment under ultraviolet radiation in the laboratory. Properties of plastic films were investigated by tensile tests, infra-red spectrometry and scanning electron microscope at various time intervals. The results showed that the elongation-at-break of six kinds of polyethylene film decreased with increasing of UV exposure time. While Young’s modulus showed a trend of increase-decrease with increasing exposure time in general. The yield strength showed a general increasing-decreasing or decreasing trend with increasing exposure time. PE films from food packing bag and degradable garbage bag became brittle and tended to break into microplasics after 36 h under UV irradiation of 160 W/m2. However, the retained elongation-at-break of PE film from express packing bag was up to 76% after 180 h UV irradiation. Chain scission and structure changes occurred during photodegradation process. FT-IR spectra indicated that difference existed in photodegraded process among PE films from six kinds of plastic bags. Ether group existed in FT-IR spectra of PE film from food packing bag, while ketone, ester, carboxylic acid, and vinyl group appeared in the spectra of thick film and express packing bag. Carbonyl index, crystallinity index and vinyl index of films from food packing bag, thick film and express packing bag increased at various degrees with prolongation of exposure time. The microstructure at tensile fracture surface became smoother after photodegradation, showing appearance of small fragments. This indicated that the intermolecular force decreased significantly, which was consistent with the trend of mechanical properties. The plastic packing bags commonly used in our daily life tend to become brittle and fragment into small pieces under ultraviolet radiation and become one source of microplastics in environment. These results can provide basic data and theoretical support for study of environmental behavior processes of plastic debris and source of microplastics, assessment of environmental risk, etc.
More Papers Like This
Photodegradation of macroplastics to microplastics : A laboratory study on common litter found in urban areas
AI summary Read the abstract
A laboratory study used UV light to simulate how plastic litter found in urban environments degrades into microplastics over time. The results help explain the pathway from discarded plastic items to the small fragments now found across the environment, from soils to human tissues.
Investigating the physicochemical property changes of plastic packaging material exposed to UV radiation
AI summary Read the abstract
UV radiation was shown to degrade polypropylene and PET plastic packaging materials, causing surface changes and potential microplastic formation, with degradation rates influenced by sample shape and size. These findings are relevant to understanding how discarded plastic packaging breaks down in marine and outdoor environments.
Investigating the Physicochemical Property Changes of Plastic Packaging Exposed to UV Irradiation and Different Aqueous Environments
AI summary Read the abstract
Researchers investigated UV-driven degradation of polypropylene and PET packaging materials under different aqueous conditions, finding that UV exposure caused significant physicochemical changes including increased crystallinity and surface cracking that contribute to microplastic formation.
Microplastics Generation: Onset of Fragmentation of Polyethylene Films in Marine Environment Mesocosms
AI summary Read the abstract
Researchers investigated how high-density polyethylene films from plastic bags fragment into microplastics under simulated beach and nearshore conditions over six months. The study found that natural sunlight exposure on sand or in seawater caused measurable degradation, providing evidence for how everyday plastic bags break down into microplastic particles in marine environments.
From macroplastics to microplastics: Role of water in the fragmentation of polyethylene
AI summary Read the abstract
Laboratory photodegradation experiments compared how polyethylene plastic films fragment in water versus air under UV light, finding that the aquatic environment significantly influences the physical and chemical breakdown of plastic into microplastics. The study improves understanding of how water immersion changes the photodegradation pathways of floating and submerged plastic debris.
Research digests by email
When a large batch of papers lands in the Atlas, we read through it and send a short write-up of what stood out.