Microplastics Generation: Onset of Fragmentation of Polyethylene Films in Marine Environment Mesocosms
AI summary Read the abstract
Researchers investigated how high-density polyethylene films from plastic bags fragment into microplastics under simulated beach and nearshore conditions over six months. The study found that natural sunlight exposure on sand or in seawater caused measurable degradation, providing evidence for how everyday plastic bags break down into microplastic particles in marine environments.
The fragmentation of high-density polyethylene (HDPE) films from single-use supermarket plastic bags to microplastics under laboratory-simulated onshore and nearshore conditions was investigated for a period of 6 months. The weathering process of the plastic strips either on beach sand or in seawater under direct natural sunlight was monitored by tensile strength, molecular weight measurements, FTIR, weight loss and image processing of photographs of the plastic strips before and after mild mechanical stress was applied. The latter represents a novel method proposed for determining the onset of fragmentation through the application of mild mechanical stress on the weathered plastic samples emulating the action of sand and wind on a beach. It was found that 12 h of application of mild mechanical stress in rotating glass bottles filled partially with sand was sufficient time to reach the maximum degree of fragmentation that could occur for the weathered plastics samples being tested. For example, applied mechanical stress yielded an area loss of almost 14% for samples weathered for a period of 5 months and about 16.7% after 5.5 months. While tensile strength tests and molecular weight measurements were rather inconclusive till the very last month when the onset of fragmentation was identified; FTIR measurements revealed that samples under ultraviolet irradiation were gradually modified chemically until fragmentation commenced. After 6 months of weathering, molecular weight measurements showed a 60% reduction for sample SMB-1 whereas for sample SMB-2 the measurement was not possible due to extensive fragmentation. The onset of fragmentation for SMB-1 and SMB-2 samples occurred at a cumulative luminance of 5.3x106 lux•d and in the presence of atmospheric oxygen whereby the polymer films broke down partially to microplastics. When the UV exposure reached 7.2x106 lux•d the weathered plastic strips broke down fully to microplastics with the application of a mild mechanical stress. Samples placed in seawater proved to be resistant to fragmentation compared to those on sand over the six-month period of the weathering experiment. The direct implication of this work is that beached macroplastic debris should be regularly collected from the seashore before they are weathered by sunlight and returned to the
More Papers Like This
Microplastics formation based on degradation characteristics of beached plastic bags
AI summary Read the abstract
Laboratory weathering of plastic bags under UV and mechanical stress produced microplastic fragments of varied sizes and shapes, with degradation rate and fragment characteristics depending on the bag material and environmental conditions.
The characteristic change of plastic film from common used packing bags under UV photodegradation
AI summary Read the abstract
Researchers studied how UV light degrades plastic packaging films over time, finding that photodegradation causes surface cracking and chemical changes that progressively break plastic into smaller fragments, including microplastics. The findings help explain how discarded plastic packaging contributes to microplastic accumulation in the marine environment.
From macroplastics to microplastics: Role of water in the fragmentation of polyethylene
AI summary Read the abstract
Laboratory photodegradation experiments compared how polyethylene plastic films fragment in water versus air under UV light, finding that the aquatic environment significantly influences the physical and chemical breakdown of plastic into microplastics. The study improves understanding of how water immersion changes the photodegradation pathways of floating and submerged plastic debris.
Evaluation of the degradation from micro to nanoplastics from biodegradable bags in marine conditions
AI summary Read the abstract
Researchers evaluated how biodegradable plastic bags degrade into micro- and nanoplastics under environmental conditions, comparing them to conventional plastics. The study found that even biodegradable materials generate persistent micro- and nanoplastic particles under real-world conditions.
From macroplastic to microplastic: Degradation of high-density polyethylene, polypropylene, and polystyrene in a salt marsh habitat
AI summary Read the abstract
Researchers subjected high-density polyethylene, polypropylene, and other plastics to simulated environmental degradation and tracked their fragmentation from macro- to microplastic sizes, characterizing surface changes and particle generation rates.