Formation of microplastic fibers and fibrils during abrasion of a representative set of 12 polyester textiles
Summary
Abrasion testing of representative polyester fabrics generated microplastic fibers and fibrils, with fiber characteristics reflecting the mechanical and chemical properties of the parent textile. The findings suggest that real-life wear and abrasion during use, not just laundering, is a significant pathway for microfiber release from synthetic textiles.
Microplastic fibers (MPFs) released from synthetic textiles have been found to be a major source of microplastic in the environment. There is increasing evidence available that MPFs released during washing were likely formed during the manufacturing stage. However, real-life use of textiles is often associated with textile-on-textile abrasion, and the first evidence is available that MPFs and finer microplastic fiber fragments (fibrils) are formed during abrasion. In this study, we characterized the formation of MPFs and fibrils from a representative set of 12 polyester textiles after abrasion tests conducted with a Martindale tester. We also investigated the influence of rub intensity and the extractability of MPFs and fibrils from the abraded fabrics. For all textiles, the MPFs extracted after abrasion showed the same diameter as the fibers in non-abraded textiles (10-20 μm), while the extracted fibrils were much thinner (3-5 μm). The variability in the structure of the different polyester textiles led to a broad range of MPF and fibrils extracted during the first wash after 5000 rubs. One gram of textile released between 4900 and 640,000 MPFs and between 0 and 350,000 fibrils with an average fibril/MPF ratio of 0.8. The total number of MPFs and fibrils formed during abrasion was positively correlated with the increase in the number of rubs up to 10,000 times. Visible pilling on the textile surface was an important indicator for the formation of MPFs and fibrils. Our study revealed that textile abrasion is a critical, realistic, and overlooked mechanism for the formation of MPFs and fibrils, as abraded textiles (after 5000 times rubs) can release more than ten times the number of MPFs and fibrils compared to washing only.
Sign in to start a discussion.
More Papers Like This
Formation of Fiber Fragments during Abrasion of Polyester Textiles
Researchers investigated how physical abrasion of polyester textiles produces microplastic fibers and found that the process generates both standard-diameter fibers and much finer fibrils, some as thin as 2.4 micrometers. The number of fibrils produced during abrasion exceeded the number of regular microplastic fibers, and abrasion released 5 to 30 times more fiber fragments than washing. The study suggests that everyday wear of synthetic clothing may be a more significant source of microplastic pollution than previously recognized.
Differences in the release of microplastic fibers and fibrils from virgin and recycled polyester textiles
Researchers compared microplastic fiber and fibril release from virgin versus mechanically recycled polyester textiles during abrasion testing. They analyzed four pairs of commercially available textiles that were identical except for the type of polyester used. The findings provide important data for understanding whether the growing use of recycled polyester in clothing changes the amount or character of microplastic shedding during wear.
Characterization of Nanoplastics, Fibrils, and Microplastics Released during Washing and Abrasion of Polyester Textiles
Researchers analyzed the full range of plastic particles released during washing and physical abrasion of polyester textiles, including nanoplastics smaller than 1000 nanometers. They found that both washing and abrasion produced substantial numbers of nanoplastics and microfibers, with abrasion generating even finer fragments. The study highlights synthetic clothing as a significant and underappreciated source of very small plastic particles entering the environment.
Characterization of microfibers released from chemically modified polyester fabrics — A step towards mitigation
This study characterized microfibers released from chemically modified polyester fabrics during abrasion, finding that surface treatments altered fiber release rates and morphology. The results inform strategies to reduce microfiber pollution from synthetic textiles at the manufacturing and use stages.
Quantifying shedding of synthetic fibers from textiles; a source of microplastics released into the environment
Researchers quantified the shedding of synthetic fibers from textiles during simulated washing, finding that fabric type, age, and wash conditions significantly affected fiber release, and establishing a quantitative basis for estimating textile-derived microplastic inputs.