Formation of Fiber Fragments during Abrasion of Polyester Textiles
Summary
Researchers investigated how physical abrasion of polyester textiles produces microplastic fibers and found that the process generates both standard-diameter fibers and much finer fibrils, some as thin as 2.4 micrometers. The number of fibrils produced during abrasion exceeded the number of regular microplastic fibers, and abrasion released 5 to 30 times more fiber fragments than washing. The study suggests that everyday wear of synthetic clothing may be a more significant source of microplastic pollution than previously recognized.
Fiber fragments are one of the dominant types of microplastics in environmental samples, suggesting that synthetic textiles are a potential source of microplastics to the environment. Whereas the release of microplastics during washing of textiles is already well studied, much less is known about the release during abrasion processes. The abrasion of textiles may induce fibrillation of fibers and therefore result in the formation of much finer fiber fragments. The aim of this study was to investigate the influence of abrasion of synthetic textiles on the formation of microplastic fibers and fibrils. Fleece and interlock textile swatches made of polyester were abraded using abrasion tests with a Martindale tester. The microplastic fibers and fibrils formed during abrasion were extracted from the textiles and characterized in terms of number, length, and diameter. The microplastic fibers demonstrated the same diameter than the fibers found in the textiles (fleece: 12.3 μm; interlock: 12.7 μm), while fibrils with a much smaller diameter (fleece: 2.4 μm; interlock: 4.9 μm) were also found. The number of fibrils formed during abrasion in both textiles was higher than the number of microplastic fibers. The majority of the extracted microplastic fibers had a length between 200 and 800 μm, while most fibrils were between 30 and 150 μm, forming two distinct fiber fragment morphologies. The number of microplastic fibers formed during abrasion was 5 to 30 times higher than the number of microplastic fibers that could be extracted from non-abraded samples. The number of fibrils increased after abrasion by more than a factor of 200 for both fabric types. The fibrils formed during abrasion have diameters that fall within the inhalable size for airborne particles. The potential release of fibrils into air during wear of textiles thus raises questions about the human exposure to these materials. Since the Martindale tester can simulate a daily application scenario of textiles over a prolonged period only in a limited way, future studies are needed to establish the correlation between the test results with a real-world scenario.
Sign in to start a discussion.
More Papers Like This
Formation of microplastic fibers and fibrils during abrasion of a representative set of 12 polyester textiles
Abrasion testing of representative polyester fabrics generated microplastic fibers and fibrils, with fiber characteristics reflecting the mechanical and chemical properties of the parent textile. The findings suggest that real-life wear and abrasion during use, not just laundering, is a significant pathway for microfiber release from synthetic textiles.
Characterization of Nanoplastics, Fibrils, and Microplastics Released during Washing and Abrasion of Polyester Textiles
Researchers analyzed the full range of plastic particles released during washing and physical abrasion of polyester textiles, including nanoplastics smaller than 1000 nanometers. They found that both washing and abrasion produced substantial numbers of nanoplastics and microfibers, with abrasion generating even finer fragments. The study highlights synthetic clothing as a significant and underappreciated source of very small plastic particles entering the environment.
Differences in the release of microplastic fibers and fibrils from virgin and recycled polyester textiles
Researchers compared microplastic fiber and fibril release from virgin versus mechanically recycled polyester textiles during abrasion testing. They analyzed four pairs of commercially available textiles that were identical except for the type of polyester used. The findings provide important data for understanding whether the growing use of recycled polyester in clothing changes the amount or character of microplastic shedding during wear.
Quantifying shedding of synthetic fibers from textiles; a source of microplastics released into the environment
Researchers quantified the shedding of synthetic fibers from textiles during simulated washing, finding that fabric type, age, and wash conditions significantly affected fiber release, and establishing a quantitative basis for estimating textile-derived microplastic inputs.
Assessment of microplastics release from polyester fabrics: The impact of different washing conditions
Researchers assessed microplastic fiber release from polyester and polyamide fabrics during simulated washing, finding that fabric construction, fiber type, and washing conditions all influenced the quantity of fibers released. The study provides data to help quantify the contribution of laundry to microplastic emissions in wastewater.