A new concept for the ecotoxicological assessment of plastics under consideration of aging processes
Summary
A new ecotoxicological assessment approach for plastic leachates derived from alternating UV and hydrolysis weathering found that polystyrene leachates produced measurable algae growth inhibition and that oxidized polymer degradation products may be more bioavailable and toxic than pristine particles.
Abstract Microplastics are widely distributed in aquatic and terrestrial environments, but up to now less is known about (eco)toxicological impacts under realistic conditions. Research so far has focused mainly on impacts on organisms by fresh, single‐origin plastic fragments or beads. However, plastics found in the environment are complex in composition, this means different polymer types and sources, with and without additives and in all stages of age, and therefore, in a more or less advanced stage of degradation. For oxidized degradation products that might be released from plastic materials during aging, there is a lack of information on potentially adverse effects on aquatic biota. The latter is of particular interest as oxidized degradation products might become more water soluble due to higher polarity and are more bioavailable, therefore. The present study focused on plastic leachates of polystyrene (PS) and polylactic acid (PLA), which were derived from alternating stress by hydrolysis and ultraviolet (UV) radiation—representing a realistic scenario in the environment. Test specimens of PS, PLA, or a PLA/PS layer (each 50%) were alternately exposed to UV radiation for 5 days followed by hydrolysis for 2 days, for several weeks alternating. Ecotoxicological effects of the storage water (artificial freshwater) of the test specimens and additionally, in a second experimental setup, the effects of five potential polymer degradation products were detected by 72 h algae growth inhibition tests with Desmodesmus subspicatus . Results clearly indicate inhibitory effects on algae growth by contaminants in the storage water of stressed plastics with increasing growth inhibition of proceeding hydrolysis and UV stress times. Different polymers caused variable inhibitions of algae growth with stronger inhibitions by PS and less effects by PLA and the mixed layer of both. Moreover, not microplastic particles but the resulting dissolved degradation products after aging caused the ecotoxicological effects—with strong effects by the oxidized degradation products. The existing data highlight the relevance of plastic aging as a framework for microplastic ecotoxicity evaluation and allow a proof of concept.
Sign in to start a discussion.
More Papers Like This
Accelerated Weathering Increases the Release of Toxic Leachates from Microplastic Particles as Demonstrated through Altered Toxicity to the Green Algae Raphidocelis subcapitata
Researchers subjected polystyrene microplastics to accelerated weathering and tested the resulting leachates against green algae, finding that weathered particles released significantly more toxic compounds and caused greater inhibition of algal growth than pristine particles.
Toxic effects of pristine and aged polystyrene and their leachate on marine microalgae Skeletonema costatum
Researchers compared the toxic effects of pristine and aged polystyrene microplastics, as well as their chemical leachates, on the marine microalga Skeletonema costatum. The study found that aged microplastics and their leachates caused greater growth inhibition, reduced chlorophyll concentration, and triggered stronger oxidative stress responses than pristine particles, suggesting that environmental weathering increases the toxicity of plastic debris.
Releasing characteristics of toxic chemicals from polystyrene microplastics in the aqueous environment during photoaging process
This study revealed that as polystyrene microplastics age under UV light, they release a growing number of toxic chemicals including organic compounds and heavy metals into surrounding water. The rate of chemical release increased dramatically with aging time, meaning that weathered microplastics in the environment are more chemically hazardous than fresh ones, with implications for water quality and human exposure.
Aging mechanism of microplastics with UV irradiation and its effects on the adsorption of heavy metals
Researchers aged polystyrene microplastics using UV irradiation under three conditions (air, pure water, seawater) and found that aging changed surface chemistry and increased the microplastics' capacity to adsorb heavy metals, with seawater aging producing the most pronounced surface oxidation.
Ecotoxicological assessment of microplastics in limnic systems with emphasis on chemicals released by weathering
This study examined both the physical and chemical toxicity of microplastics in freshwater ecosystems, with special focus on chemicals released when plastics are weathered by ultraviolet light. The research tested conventional and biodegradable plastics, addressing whether particle properties or leaching chemicals drive ecotoxicological effects.