From cracks to secondary microplastics - surface characterization of polyethylene terephthalate (PET) during weathering
Summary
Scientists tracked how PET plastic, the material used in water bottles and clothing, develops cracks and eventually breaks into microplastics during exposure to UV light and water. Different forms of PET broke down in different ways and at different speeds, with water-submerged samples showing organized crack networks within 30 days. The study helps explain how everyday plastic products fragment into the microplastics found throughout the environment, with fibers being one of the most common shapes produced.
Secondary microplastics are a product of the fragmentation of plastic debris. Despite concerns regarding the omnipresence of microplastics in the environment, knowledge about the mechanics of their actual formation is still limited. Fragmentation is usually linked to weathering, which alters the properties of the plastic and allows fragmentation to occur. Therefore, in this study, polyethylene terephthalate (PET) samples were exposed to artificial UV light or a combination of UV light and water for a total of three months to simulate natural weathering. The samples included three forms of PET with different production histories: pellets, yarns, and films. The surface alterations to the samples during weathering were characterized using scanning electron microscopy and Raman spectroscopy. Results indicated that the three different types of PET developed markedly different surface defects and also exhibited signs of weathering within different time frames. Differences were also found between samples exposed only to UV and those exposed to UV and submerged in water. In water, the first surface changes were spotted within 30 days of initial submersion and later developed into an organized crack network. Upon the introduction of mild mechanical forces, pieces of the weathered surface started to delaminate. The fragments from films had an elongated shape with a median size of 16.1 × 2.1 × 1.8 μm, resembling a fibre. If the weathered surface of a film were to detach completely, it could create 1.4-7.9 million microplastic fragments/cm2. For pellets, this number would range between 0.4 and 2.2 million microplastics/cm2. In addition to particle formation by surface delamination, particles also emerged on the weathered surfaces of all studied samples, presenting another possible source of micro-sized particles during weathering. Overall, the results of this work show that the weathering of plastics and the formation of microplastics are heavily influenced not only by the weathering mechanism but also by the type and production history of the polymers.
Sign in to start a discussion.
More Papers Like This
Photo-induced degradation of single-use polyethylene terephthalate microplastics under laboratory and outdoor environmental conditions
Researchers tested how sunlight, water, and physical wear work together to break down PET microplastics, the type commonly found in plastic bottles and food packaging. Over 60 days, combined UV light and water exposure caused significant chemical degradation of the plastic surfaces. This matters because as microplastics break down in the environment, they release smaller fragments and potentially harmful chemicals that are easier for organisms to absorb.
Rheological Characterization of UV and Shear‐Induced Degradation of Poly(Ethylene Terephthalate): Linking Environmental and Processing Histories to Recyclability
Researchers studied how UV light exposure and mechanical processing degrade PET plastic at the molecular level. They found that UV aging in water environments causes the plastic chains to break apart, while dry conditions promote crosslinking, and that even a single round of recycling processing dramatically reduces crystal size and releases volatile byproducts. The study reveals that both environmental weathering and recycling significantly weaken PET's mechanical properties, which has implications for both microplastic generation and plastic recyclability.
Changes in the Chemical Composition of Polyethylene Terephthalate under UV Radiation in Various Environmental Conditions.
Researchers exposed polyethylene terephthalate (PET) to UV radiation under controlled humidity conditions and tracked changes in its chemical composition, finding progressive oxidation and chain scission that alter the polymer's surface properties. Understanding how PET degrades under UV exposure is important for predicting how PET microplastics form and what chemical changes make them more or less bioavailable.
Investigating the Physicochemical Property Changes of Plastic Packaging Exposed to UV Irradiation and Different Aqueous Environments
Researchers investigated UV-driven degradation of polypropylene and PET packaging materials under different aqueous conditions, finding that UV exposure caused significant physicochemical changes including increased crystallinity and surface cracking that contribute to microplastic formation.
Degradation of Polyethylene Terephthalate (pet) as Secondary Microplastics Under Three Different Environmental Conditions
Researchers investigated the degradation of PET bottles used as biofilm media in wastewater treatment plants under indoor, outdoor, and UV-irradiated conditions over seven months, measuring secondary microplastic generation. They found that UV irradiation dramatically accelerated PET fragmentation, with microplastic concentrations rising from 15 particles per liter at month one to nearly 249 particles per liter by month seven, with fragments and transparent particles dominating.