Statistical optimization of process variables for improved poly(ethylene terephthalate) plastic degradation by a rhizospheric bacterial consortium
AI summary Read the abstract
Researchers optimized conditions for a rhizobacterial consortium to degrade PET plastic powder, achieving 71% weight reduction over 18 days at controlled temperature and pH, with FTIR and SEM analyses confirming structural changes to the plastic surface.
The current study focuses on the poly(ethylene terephthalate) (PET) powder degradation potential of a rhizobacterial consortium screened from the rhizosphere of plants growing at plastic-polluted sites. The rhizobacterial consortium were screened and ability of PET powder degradation was studied up to 18 days. For observing the efficiency of degradation, all three rhizobacterial strains with highest percentage of degradation were combined to formulate the consortium. The Response Surface Methodology (RSM) was used to optimize the process variables. The combinations demonstrating highest weight reduction percentage for PET were selected for further degradation studies. The changes in the structure and surfaces that occurred after biodegradation on the plastic were observed through SEM and FTIR analysis. The obtained results showed the disappearance and elongation of the peak, signifying that the rhizobacterial consortium could modify the PET plastic. The weight reduction percentage of PET powder (300 µm) was 71.12% at optimized conditions (29.8 °C, 7.02 pH and 1 g/L carbon source). The mathematical model developed through RSM is found to be significant (P < 0.05), and optimization and validation experiments were also well correlated for the process.
More Papers Like This
Biodegradation of polyethylene terephthalate microplastics by Paenibacillus naphthalenovorans PETKKU2: Response surface optimization and genomic evidence for an alternative degradation mechanism
AI summary Read the abstract
This study identified a soil bacterium, Paenibacillus naphthalenovorans PETKKU2, isolated from a Thai landfill, as capable of degrading PET microplastics and achieving nearly 10% weight loss over 35 days under optimized conditions — through a degradation pathway distinct from the well-known PETase enzyme route. Surface analysis confirmed progressive erosion and chemical changes in the plastic. Discovering new microbial pathways for PET degradation is important for developing biological recycling and remediation strategies for one of the world's most common plastic pollutants.
Biological Degradation of Polyethylene Terephthalate by Rhizobacteria
AI summary Read the abstract
Researchers isolated rhizobacteria — bacteria associated with plant roots — that can biodegrade polyethylene terephthalate (PET) plastic. This finding suggests that soil bacteria near plants may contribute to plastic breakdown in contaminated soils, though degradation rates remain slow.
Potensi Biodegradasi Platik PET (Polyethylene Terephthalate) Menggunakan Mikroorganisme Tanah TPA dengan Metode Kolom Winogradsky
AI summary Read the abstract
A Winogradsky column experiment using landfill soil microorganisms achieved up to 0.196% mass reduction of PET plastic in 60 days, with FTIR confirming structural degradation indicated by shifting C–O bond ratios. This study contributes to understanding biological PET degradation pathways, which is important for evaluating whether natural microbial communities can reduce microplastic accumulation in landfill environments.
Different aspects of bacterial polyethylene terephthalate biodegradation
AI summary Read the abstract
This study reviews how bacteria degrade polyethylene terephthalate (PET) plastic by breaking it down into terephthalic acid and ethylene glycol through the action of PET hydrolase enzymes. While bacterial biodegradation offers an eco-friendly alternative to landfilling or incineration, limitations such as low enzyme stability and inhibition by degradation intermediates must be overcome through genetic and enzyme engineering.
Biodegradation of PET Microplastics by Bacteria
AI summary Read the abstract
This Spanish-language study tested the ability of common bacterial strains (E. coli, C. freundii, P. vulgaris, E. aerogenes) to biodegrade PET microplastics, achieving biodegradation rates of 87-95% in minimal mineral medium, demonstrating that microbial consortia can efficiently break down plastic contaminants. These findings are directly relevant to microplastic pollution research, offering a bioremediation pathway for one of the most prevalent plastic polymers found in aquatic and terrestrial environments.