Degradation of Plastics in Simulated Landfill Conditions
Summary
Researchers exposed high-density polyethylene, oxo-degradable polyethylene, and certified compostable plastics to simulated landfill conditions for 854 days and found that only compostable plastic degraded substantially, while oxo-degradable plastic showed minimal improvement over standard HDPE under anaerobic landfill conditions.
Different degradable plastics have been promoted as a solution for the accumulation of waste in landfills and the natural environment; in Mexico, the most popular options are oxo-degradable, which degrade in a sequential abiotic–biotic process, and compostable plastics. In this research, high-density polyethylene, oxo-degradable high-density polyethylene, and certified compostable plastic were exposed to simulated landfill conditions in an 854-day-long experiment to assess their degradation. High-density polyethylene showed limited degradation, due mainly to surface erosion, evidenced by a 13% decrease in elongation at break. The pro-oxidant additive in the oxo-degradable plastic increased this loss of mechanical properties to 27%. However, both plastic films kept their physical integrity and high molecular weight by the end of the experiment, evidencing degradation but no biodegradation. While the compostable film fragmented, had a lower molecular weight at the end of the experiment, and decreased the presence of C=O bonds, this degradation took place remarkably slower than expected from a composting process. Results show that oxo-degradable and compostable plastics will not biodegrade readily in landfills. This fact should be known and understood for decision-makers to match the characteristics of the materials to the features of the waste management systems.
Sign in to start a discussion.
More Papers Like This
Biodegradable plastics in the air and soil environment: Low degradation rate and high microplastics formation
Researchers compared the degradation rates of various biodegradable plastic types in natural air and soil environments over time, finding that most degraded slowly under ambient conditions and generated substantial microplastic fragments, with non-certified biodegradable plastics showing essentially no degradation.
Degradation of supposedly biodegradable polymers in a real estuarine environment
Researchers tested the real-world degradation of supposedly biodegradable polymer bags in an estuarine environment over 180 days. The study found that bags made of PLA combined with PBAT and starch showed the most consistent degradation, while polyethylene bags with oxo-biodegradable additives and plain polyethylene showed minimal breakdown, questioning the effectiveness of some biodegradable alternatives in natural settings.
The degradation of single-use plastics and commercially viable bioplastics in the environment: A review
Researchers reviewed how conventional single-use plastics degrade over decades in natural environments versus how bioplastics biodegrade, finding that while alternatives like PBS and PHA show genuine biodegradation potential, most require specific industrial composting conditions that are rarely available in practice.
Biodegradation of plastic wastes under semi-aerobic condition with active methane oxidation activities and nutrient supply
Researchers tested biodegradation of plastic wastes under semi-aerobic landfill conditions, finding that polymer type and landfill conditions strongly influenced degradation rates and the generation of microplastic fragments. The study contributes to understanding how managed disposal sites affect long-term plastic persistence.
Biodegradability of Plastics: Challenges and Misconceptions
This review addresses widespread misconceptions about plastic biodegradability, explaining why most plastics persist in the environment for decades to centuries despite industry marketing claims. It clarifies the distinction between degradable, biodegradable, and compostable plastics and explains why real-world conditions rarely support plastic breakdown.