Mechanical Properties and Microstructure of Epoxy Mortars Made with Polyethylene and Poly(Ethylene Terephthalate) Waste
Summary
Researchers incorporated recycled PET and polyethylene waste into epoxy mortars, finding that plastic waste could partially replace conventional materials without significantly reducing strength properties. The modified mortars also had lower bulk density, potentially making them useful in lightweight construction applications.
The article describes the results of a study to determine the simultaneous effect of polyethylene terephthalate waste (PET) and polyethylene (PE) on the strength characteristics and bulk density of epoxy mortars. In these mortars, 9 wt.% of the polymer binder was replaced by glycolysate which was made from PET waste and propylene glycol. Additionally, 0-10 vol.% of the aggregate was substituted with PE agglomerate made from plastic bags waste, respectively. The modification of the composition of epoxy mortar has a special environmental and economic aspect. It also allows to protect natural sources of the aggregate, while reducing the amount of waste and reducing problems arising from the need to store them. The resulting composite has very good strength properties. With the substitution of 9 wt.% of resin and 5 vol.% of sand, a flexural strength of 35.7 MPa and a compressive strength of 101.1 MPa was obtained. The results of the microstructure study of the obtained mortars constitute a significant part of the paper.