Process analysis of microplastic degradation using activated PMS and Fenton reagents
Summary
Researchers demonstrated that activated peroxymonosulfate and Fenton reagents can degrade nylon and polystyrene microplastics through free radical oxidation, achieving mass losses exceeding 20% after four treatment cycles.
The environmental degradation and physical aging of microplastics (MP) caused by oxidative stress have not been thoroughly elucidated. In this study, we used different oxidative agents (Fe-activated peroxymonosulfate and Fenton reagents) that can form free radicals to study the degradation mechanisms of nylon 6 (PA6) and polystyrene (PS) MPs. After 4 cycles of treatment, mass losses of 25.6% and 22.1% were obtained with PA6 and PS MPs, respectively. Scanning electron microscopy (SEM), Fourier-transform infrared (FTIR) spectroscopy, Raman spectroscopy, and X-ray photoelectron spectroscopy (XPS) were employed to confirm the MP oxidation, and polymer chain scissions. FTIR data indicated the existence of oxygen-containing chemical groups resulting from MPs oxidation, and chain scissions, such as CO, C-O, and O-CO. Raman spectroscopy suggested the presence of exposed aromatic groups, and weakening of the relative intensity of C-H related to the oxidation, and chain scission of the MPs. SEM imaging revealed visible morphological changes on the surface of MPs as a result of degradation. XPS indicated that the O/C ratio could be used as an indicator for the degree of MPs oxidation. By analyzing the degradation products with surface-enhanced Raman scattering (SERS) and gas chromatography-mass spectrometry, low-molecular-weight alkanes, alcohols, aldehydes, carboxylic acids derived from the derivatization of alcohols, were detected. These findings confirmed the advantage of using multiple analytic methods in tandem to evaluate the degradation of environmental MPs.
Sign in to start a discussion.
More Papers Like This
Insights into the degradation of microplastics by Fenton oxidation: From surface modification to mineralization
Researchers investigated Fenton oxidation of five common microplastic types, finding that while bulk particles showed modest weight losses of around 10%, polystyrene nanoplastics achieved 70% mineralization, with aromatic polymers being more susceptible to degradation.
Effects of advanced oxidation processes on leachates and properties of microplastics
Ozonation, Fenton, and heat-activated persulfate treatments were applied to microplastics containing pigment red, finding that all three advanced oxidation processes effectively degraded the released pigment and altered nanoscale surface properties of the treated MPs.
Photo-fenton oxidation of microplastics: Impact of polymer nature
Researchers investigated photo-Fenton oxidation as a treatment for microplastics, finding that degradation efficiency varies significantly by polymer type. Polymers with aromatic structures and those with greater oxidative susceptibility degraded more rapidly under photo-Fenton conditions.
Mechanisms of polystyrene microplastic degradation by the microbially driven Fenton reaction
Researchers demonstrated that polystyrene microplastics can be continuously degraded through the microbially driven Fenton reaction using Shewanella putrefaciens, revealing that bacteria produce protective biofilms to withstand hydroxyl radical damage while maintaining their degradation capacity.
Photo-fenton oxidation of microplastics: Impact of polymer nature
Researchers tested photo-Fenton oxidation as a treatment method for microplastics, comparing degradation efficiency across different polymer types. The study found that polymer chemistry significantly influences how quickly microplastics break down under this oxidative treatment.