Controlled and Accelerated Hydrolysis of Polylactide (PLA) through Pentaerythritol Phosphites with Acid Scavengers

This study provides insight into the accelerated hydrolysis of polyester PLA through the addition of phosphites based on pentaerythritol. To control hydrolysis and ensure processing stability, different types of phosphites and combinations of phosphites with acid scavengers were studied. Therefore, commercially available PLA was compounded with selected additives on a twin-screw extruder, and hydrolysis experiments were performed at 23 °C, 35 °C and 58 °C in deionized water. Hydrolysis of PLA was evaluated by the melt volume rate (MVR) and size-exclusion chromatography (SEC). For example, after 4 days of water storage at 58 °C, the number average molecular weight of the PLA comparison sample was reduced by 31.3%, whereas PLA compounded with 0.8% phosphite P1 had a 57.7% lower molecular weight. The results are in good agreement with the expected and tested stability against hydrolysis of the investigated phosphite structures. 31P-NMR spectroscopy was utilized to elucidate the hydrolysis of phosphites in the presence of lactic acid. With the addition of phosphites based on pentaerythritol, the hydrolysis rate can be enhanced, and faster biodegradation behavior of biodegradable polyesters is expected. Accelerated biodegradation is beneficial for reducing the residence time of polymers in composting facilities or during home composting and as litter or microplastic residues.