H2O2 concentration influenced the photoaging mechanism and kinetics of polystyrene microplastic under UV irradiation: Direct and indirect photolysis
No summary available — this paper's abstract is not included in the open metadata provided by the publisher. Learn why →
More Papers Like This
Investigation of Surface Alteration of Microplastics by Using UV Irradiation
AI summary Read the abstract
UV radiation causes polystyrene and other plastic microparticles to undergo photooxidative degradation, changing their surface chemistry and potentially making them more likely to adsorb or release chemical pollutants. Understanding these weathering processes is important for predicting the environmental behavior and toxicity of microplastics.
Exploring the mechanisms of humic acid mediated degradation of polystyrene microplastics under ultraviolet light conditions
AI summary Read the abstract
Humic acid in water promoted the photodegradation of polystyrene microplastics under UV light by generating higher levels of hydroxyl radicals (0.631 mM), resulting in 4.3% greater weight loss, smaller average particle size (89.5 microns), and more oxygen-containing products compared to UV alone.
Photoaging of Polyvinyl Chloride and Polystyrene Under UVA Radiation in Diverse Environmental Conditions
AI summary Read the abstract
Researchers exposed polyvinyl chloride and polystyrene plastics to UVA radiation under diverse environmental conditions and tracked their photoaging and fragmentation, finding that UVA exposure accelerates microplastic generation in ways that vary with environmental context.
High salinity promotes the photoaging of polystyrene microplastics with humic acid in seawater
AI summary Read the abstract
Researchers found that high salinity seawater significantly accelerates the photoaging of polystyrene microplastics in the presence of humic acid, producing more hydroxyl radicals that promote fragmentation and oxidation of the plastic particles.
Which factors mainly drive the photoaging of microplastics in freshwater?
AI summary Read the abstract
This study systematically investigated the roles of UV irradiation, oxygen, temperature, and physical abrasion in the photoaging of polystyrene microplastics in freshwater. UV irradiation and mechanical abrasion were identified as the dominant aging factors, and their combined effect caused more extensive surface oxidation and fragmentation than either alone.