Enhanced Adsorption of Bromoform onto Microplastic Polyethylene Terephthalate Exposed to Ozonation and Chlorination
Summary
Researchers found that ozonation and chlorination of polyethylene terephthalate microplastics increased their surface hydrophilicity and carbonyl groups, significantly enhancing their adsorption capacity for the disinfection by-product bromoform.
This paper selected microplastic polyethylene terephthalate (PET), commonly found in water/wastewater plant effluent, to investigate the changes of PET oxidized under ozonation (designated as ozonized PET), followed by sodium hypochlorite oxidation (designated as ozonized-chlorinated PET) and studied their influence on the adsorption of the disinfection by-product bromoform (TBM). Fragmentation and cracks appeared on the oxidized PET surface. As the oxidation degree increased, the contact angle decreased from 137° to 128.90° and 128.50°, suggesting hydrophilicity was enhanced. FTIR and XPS analyses suggested that carbonyl groups increased on the surface of ozonized PET and ozonized-chlorinated PET, while the formation of intermolecular halogen bonds was possible when PET experienced dual oxidation. These physiochemical changes enhanced the adsorption of TBM. The adsorption capacity of TBM followed the order of ozonized-chlorinated PET (2.64 × 10−6 μg/μg) > ozonized PET (2.58 × 10−6 μg/μg) > pristine PET (2.43 × 10−6 μg/μg). The impact of raw water characteristics on the adsorption of TBM onto PETs, such as the pH, and the coexistence of inorganic ions and macromolecules (humic acid, surfactant, and bovine serum albumin) were studied. A different predominant adsorption mechanism between TBM and pristine PET or oxidized PETs was proposed.
Sign in to start a discussion.
More Papers Like This
The effect of Ozonation on the chemical structure of microplastics
Ozone treatment of microplastics in water caused oxidative changes to polymer surfaces including carbonyl group formation and surface cracking, which altered hydrophobicity and potentially increased the capacity of treated particles to adsorb contaminants, suggesting that ozonation in water treatment may chemically transform rather than eliminate microplastic hazards.
Physicochemical changes in microplastics and formation of DBPs under ozonation
Researchers examined physicochemical changes in thermoplastic polyurethane and polyethylene microplastics during ozonation water treatment, finding that the process can alter microplastic morphology and potentially generate disinfection byproducts.
Effects of microplastics on the removal of trace organic compounds during ozonation: Oxidation and adsorption of trace organic compounds and byproducts
Microplastics were found to interfere with the ozonation of trace organic compounds in water treatment, with plastic surfaces adsorbing both target pollutants and ozonation byproducts, potentially reducing treatment effectiveness and creating new exposure pathways.
Surface modification of polyethylene microplastic particles during the aqueous-phase ozonation process
Researchers examined the surface modification of polyethylene microplastics during aqueous-phase ozonation, finding that increasing ozone dosage and exposure time progressively increased carbonyl and hydroxyl functional groups on the particle surface. FTIR and XPS analysis showed ozonation altered the surface chemistry of polyethylene microplastics in ways that could change their environmental fate and pollutant adsorption capacity.
Effect of ozonation on the morphological characteristics and adsorption behavior of polystyrene microplastics in aqueous environments
Researchers exposed polystyrene microplastics to ozone treatment and found that the aging process made the particles smaller, more negatively charged, and better at absorbing pollutants from water — meaning weathered microplastics in the environment may carry more harmful chemicals than fresh ones.