Explication of mechanism governing atmospheric degradation of 3D-printed poly(lactic acid) (PLA) with different in-fill pattern and varying in-fill density
Summary
Researchers studied the atmospheric degradation of 3D-printed polylactic acid (PLA) samples exposed to natural weather conditions in India, examining different in-fill patterns and densities. The study found that while PLA performance deteriorated over time due to UV exposure, humidity, and other environmental factors, the combination of in-fill pattern and volume played an important role in the rate of degradation.
With the popularity of 3D-printing technology, poly(lactic acid) (PLA) has become a very good option for layer by layer printing as it is easy to handle, environment friendly, has low costs and most importantly, it is highly adaptable to different materials including carbon, nylon and some other fibres. PLA is an aliphatic poly-ester that is 100% bio-based and is bio-degradable as well. It is one of the rare bio-polymers to compete with traditional polymers in terms of performance and environmental impact. However, PLA is sensitive to water and susceptible to degradation under natural conditions of ultra-violet rays (UV), humidity, fumes, etc. There are many reports on the bio-degradation and photo-degradation of PLA which deal with the accelerated weathering test. However, the accelerated weathering test instruments lack the ability to correlate the stabilities maintained by the test with the actual occurrences during natural exposure. Thus, an attempt has been made in the present work to expose the 3D-printed PLA samples to actual atmospheric conditions of Aurangabad city (M.S.) in India. The degradation of PLA after the exposure is studied and a mechanism is elucidated. Additionally, the tensile properties of the PLA samples are evaluated to correlate the extent of degradation and the material performance. It was found that though the performance of PLA deteriorates with the exposure time, the combination of in-fill pattern and volume plays an important role on the tensile properties and the extent of degradation. It is concluded herein that with natural exposure, the degradation of PLA occurs in two stages, supported by a side reaction. Thus, this study offers a new perspective towards the life of components in actual application by exposing PLA to the natural atmosphere and evaluating its strength and structure.
Sign in to start a discussion.
More Papers Like This
Investigation of the Hydrolytic Degradation Kinetics of 3D-Printed PLA Structures under a Thermally Accelerated Regime
Researchers investigated the hydrolytic degradation kinetics of 3D-printed PLA structures under thermally accelerated conditions, finding that print orientation and layer thickness influence degradation rate and that PLA retains structural integrity longer than expected under moderate temperature and humidity.
The aging behavior of degradable plastic polylactic acid under the interaction of environmental factors
Researchers used response surface methodology to study how temperature, light, and humidity interact to accelerate the aging and breakdown of polylactic acid, a common biodegradable plastic. The study found that humidity had the greatest effect on PLA degradation, followed by light and temperature. Evidence indicates that even biodegradable plastics can release microplastic particles as they age under environmental conditions, posing potential ecological concerns.
3D-printed polylactic acid biopolymer and textile fibers: comparing the degradation process
3D-printed polylactic acid (PLA) objects and PLA textile fibers were compared in their degradation behavior under composting and environmental conditions. Both materials degraded over time but at different rates depending on their physical form and surface area. The study provides insights into how PLA-based products break down and whether they produce persistent microplastic residues.
Impact of moisture on the degradation and priming effects of poly(lactic acid) microplastic
Researchers examined how soil moisture levels affect the degradation of biodegradable poly(lactic acid) microplastics and their influence on soil organic carbon decomposition. The study found that moisture significantly increased PLA degradation in acidic soils, and PLA induced both positive and negative priming effects on native soil carbon depending on moisture levels and soil type.
Aging Process of Biocomposites with the PLA Matrix Modified with Different Types of Cellulose
Researchers prepared polylactic acid composites with three different cellulose-based fillers and studied how they age under UV light exposure. The study found that the type of cellulose additive plays a crucial role in how well the material resists UV degradation, with some forms improving both mechanical properties and degradation timing. These findings support the potential of biodegradable polymer composites as alternatives to conventional plastics that generate persistent microplastic waste.