Aging of PS/PVC by UV-Fenton reaction and their potential photodegradation driven in the goethite/haematite constructed wetlands
Summary
Researchers investigated UV-Fenton degradation of polystyrene and polyvinyl chloride microplastics in simulated wetland conditions, finding that combined UV and Fenton reactions achieved weight loss rates of 28.3% for PS and 35.6% for PVC — significantly higher than UV alone — while also stimulating microbial communities capable of degrading polycyclic aromatic hydrocarbon byproducts.
As the wetland ecosystem is a potential sink of plastics pieces, the photodegradation of microplastics could be boosted by iron(hydr) oxides, which considered as the Fenton or Fenton-like reactions induced. However, the pathways and internal mechanisms by which iron(hydr) oxides enhanced the ultraviolet degradation of plastics in the wetlands remain unclear. Therefore, the degradation of polystyrene (PS) and polyvinyl chloride (PVC) under ultraviolet light (365 nm) was studied in the UV Fenton and simulated micro wetlands. Results showed that UV irradiation caused notable changes in the surface morphology of plastics. Fenton reaction led to more significant, and generated oxygen-containing functional groups such as C = O. The weight loss rate of PS reached 28.3 ± 6.64%, while PVC reached 35.6 ± 1.52%, significantly surpassing the individual conditions of UV light at 20.3 ± 1.66% and 20.98 ± 8.48%, respectively. The mechanism of •OH in the process of plastic degradation was elucidated, while analysis of the degradation products was conducted. The potential risks for the UV degradation of PS and PVC were explored in constructed wetlands by detecting the changes of microbes. After preliminary aging, microbial activity associated with the degradation of polycyclic aromatic hydrocarbon compounds produced during plastic degradation is enhanced. Therefore, there may exist microbial communities in wetland ecosystems that are capable of degrading plastic. This study supported a hypothesis that the goethite/haematite Microcosm Constructed Wetlands (MCWs) would be efficiency for the degradation of plastic. It would be proved further and the organic carbon releasing during the plastic degradation should also be focused on.
Sign in to start a discussion.
More Papers Like This
Aging of PS/PVC by UV-Fenton reaction and their potential photodegradation driven in the goethite/haematite constructed wetlands
Researchers investigated the UV-Fenton-driven photodegradation of polystyrene and polyvinyl chloride microplastics in simulated constructed wetlands with goethite and haematite, finding that the Fenton reaction significantly accelerated weight loss (28.3% for PS and 35.6% for PVC) compared to UV alone, with hydroxyl radicals identified as the primary degradation mechanism and enhanced microbial activity observed toward polycyclic aromatic hydrocarbon breakdown products.
Aging of PS/PVC by UV-Fenton reaction and their potential photodegradation driven in the goethite/haematite constructed wetlands
Researchers investigated the UV-Fenton-driven photodegradation of polystyrene and polyvinyl chloride microplastics in simulated constructed wetlands with goethite and haematite, finding that the Fenton reaction significantly accelerated weight loss (28.3% for PS and 35.6% for PVC) compared to UV alone, with hydroxyl radicals identified as the primary degradation mechanism and enhanced microbial activity observed toward polycyclic aromatic hydrocarbon breakdown products.
The photodegradation processes and mechanisms of polyvinyl chloride and polyethylene terephthalate microplastic in aquatic environments: Important role of clay minerals
Researchers found that clay minerals like kaolinite and montmorillonite play an important role in the photodegradation of PVC and PET microplastics in aquatic environments, either accelerating or modifying UV-driven weathering processes.
Characteristics analysis of plastisphere biofilm and effect of aging products on nitrogen metabolizing flora in microcosm wetlands experiment
Researchers placed three types of plastic in miniature constructed wetlands for 180 days and tracked how they aged and affected microbial communities. The plastics degraded at different rates, with PVC developing new chemical groups and all surfaces becoming less water-repellent as bacteria colonized them. The plastic surfaces altered nitrogen-processing bacteria in the wetland water, suggesting microplastics can disrupt nutrient cycling in natural wetland ecosystems.
Photoaging of Polyvinyl Chloride and Polystyrene Under UVA Radiation in Diverse Environmental Conditions
Researchers exposed polyvinyl chloride and polystyrene plastics to UVA radiation under diverse environmental conditions and tracked their photoaging and fragmentation, finding that UVA exposure accelerates microplastic generation in ways that vary with environmental context.