UV-photoaging behavior of polystyrene microplastics enhanced by thermally-activated persulfate
AI summary Read the abstract
Researchers found that thermally-activated persulfate combined with UV irradiation significantly accelerated the photoaging of polystyrene microplastics, increasing surface cracking, size reduction, and contaminant adsorption capacity while generating more toxic aging byproducts.
Aging of microplastics (MPs) under natural conditions takes several months or even years. In this study, polystyrene MPs (PS-MPs) were used as the target MPs, and these were subject to artificially accelerated aging by UV irradiation (UV254) and UV/heat-activated persulfate (UV+K2S2O8). The physicochemical characteristics of aged MPs and the interaction with tetracycline hydrochloride (TH) were investigated. Simultaneously, the fluorescence characteristics, total organic carbon content (TOC), and toxicity effects of aging filtrate were also evaluated. Furthermore, the aging path of PS-MPs was derived with reactive species analysis using an electron paramagnetic resonance (EPR) test. The results showed that obvious cracks appeared on the surface of the aged PS-MPs, with the average particle size decreasing from 83.95 ± 19.93 µm to 60.41 ± 19.58 µm in the UV treatment and to 48.02 ± 18.83 µm in the UV+K2S2O8 treatment. The oxygen-containing functional groups of aged MPs were detected after the UV and UV+K2S2O8 treatment; the carbonyl index (CI) values were 0.44 and 0.62, respectively. The TH adsorption capacity of UV-treated MPs and UV+K2S2O8-treated MPs increased from 0.176 mg g−1 for pristine MPs to 0.193 mg g−1 and 0.225 mg g−1, respectively. Especially, the TOC and luminescent inhibition toxicity of the filtrate increased after aging. EPR analysis demonstrated that SO4•− and ROS played a key role in accelerating the aging of PS-MPs. This study provided a reference for UV photoaging behavior of MPs enhanced by activated K2S2O8, which is meaningful for a comprehensive understanding of MPs behavior and the risks they introduce into the environment.
More Papers Like This
The aging behavior of polyvinyl chloride microplastics promoted by UV-activated persulfate process
AI summary Read the abstract
Researchers investigated UV-activated persulfate as an accelerated aging process for PVC microplastics, finding significant dechlorination and surface changes that help predict long-term weathering behavior of microplastics in the environment.
Investigation of Surface Alteration of Microplastics by Using UV Irradiation
AI summary Read the abstract
UV radiation causes polystyrene and other plastic microparticles to undergo photooxidative degradation, changing their surface chemistry and potentially making them more likely to adsorb or release chemical pollutants. Understanding these weathering processes is important for predicting the environmental behavior and toxicity of microplastics.
Aging mechanism of microplastics with UV irradiation and its effects on the adsorption of heavy metals
AI summary Read the abstract
Researchers aged polystyrene microplastics using UV irradiation under three conditions (air, pure water, seawater) and found that aging changed surface chemistry and increased the microplastics' capacity to adsorb heavy metals, with seawater aging producing the most pronounced surface oxidation.
Wastewater preinteraction accelerates the photoaging of disposable box-derived polystyrene microplastics in water
AI summary Read the abstract
Researchers found that pre-exposure of polystyrene microplastics to real wastewater significantly accelerated their subsequent photoaging under UV light — doubling oxidation rates — with fulvic acid identified as the primary wastewater constituent driving this enhancement.
Aging of polystyrene microplastics by UV/Sodium percarbonate oxidation: Organic release, mechanism, and disinfection by-product formation
AI summary Read the abstract
Researchers studied how polystyrene microplastics break down under UV-activated sodium percarbonate oxidation, an advanced water treatment process. The study found that this treatment significantly accelerated microplastic aging and fragmentation while releasing dissolved organic matter that could serve as a precursor for disinfection byproducts during chlorination. Evidence indicates that water treatment processes may inadvertently generate secondary contaminants from microplastic degradation.