An assessment of methods used for the generation and characterization of cryomilled polystyrene micro- and nanoplastic particles

Abstract There is a critical need to generate environmentally relevant microplastics (MPs) and nanoplastics (NPs) to better investigate their behavior in laboratory settings. Environmental MPs are heterogenous in size and shape, unlike monodisperse and uniform microspheres commonly used as surrogates. Cryogenic grinding, or cryomilling, was successfully utilized to transform polystyrene (PS) bulk material into heterogenous micro and nano fragments. Fourier-Transform Infrared (FTIR) spectroscopy confirmed that this approach did not alter polymer surface chemistry. The number of milling cycles (time of milling) and frequency of grinding (intensity of milling) were varied to investigate the role cryomilling parameters had on generated MP characteristics. The resulting particle size distributions of cryomilled samples were measured and compared. Coulter Counter and Nanoparticle Tracking Analysis (NTA) were used to measure the particle size distributions at the micro and nanoparticle size ranges, respectively. Microspheres were used to determine what camera settings yielded more accurate sizing and to reduce bias in the NTA analysis. Increasing milling cycles generally increased the number of smaller particles. The evolution of the measured size distributions indicated that small nanosized fragments broke off from larger MPs during cryomilling, steadily eroding larger MP fragments. The number of milling cycles was observed to more consistently impact the size distributions of fragments compared to the frequency of milling. This study offers both analysis of the cryomilling process and recommendations for generating more realistic PS MP/NPs for examining environmental fate and effects.