Chemical/photochemical functionalization of polyethylene terephthalate fabric: effects on mechanical properties and bonding to nitrile rubber
Summary
Researchers compared two methods for modifying the surface of polyethylene terephthalate (PET) fabric — a common plastic used in textiles — to improve how it bonds to rubber, finding that UV-light-based carboxylation created 4.5 times more surface hydroxyl groups and improved adhesion by up to 33%, while chemical hydrolysis with sodium hydroxide weakened the fabric's tensile strength. The UV method offers a more effective approach for manufacturing durable rubber-plastic composite materials.
The aim of this work is to compare the effects of chemical and photochemical functionalization on the mechanical properties of PET fabric and its adhesion to nitrile rubber (NBR). The photochemical functionalization was performed by UV irradiation of PET fabric in the presence of glutaric acid peroxide at a temperature of 60 °C for different exposure times (i.e. 60, 90 and 120 min). The chemical functionalization (i.e. hydrolysis) of PET fabrics was performed by NaOH solution at a temperature of 60 °C for different times (i.e. 60, 120, 240 and 360 min). The tensile properties of the functionalized fibers were also evaluated. The functionalized PETs were evaluated for H-pull and T-peel adhesion to NBR. It was found that both treatment methods created functional groups on the PET surface. However, carboxylation of PET under GAP/UV irradiation generated much more OH groups on the PET surface (i.e. 4.5 times). The hydrolysis of PET in NaOH solution for more than 60 min caused a significant decrement in the tensile strength contrary to carboxylation under GAP/UV irradiation. It was also found that pullout and T-peel adhesions to NBR decreased in the case of hydrolysis of PET while they increased about 33 and 12% for GAP/UV irradiated PET, respectively.
Sign in to start a discussion.
More Papers Like This
Vacuum UV (VUV) Photo‐Oxidation of Polymer Surfaces to Enhance Adhesion
Not relevant to microplastics — this paper reviews vacuum UV photo-oxidation techniques for improving adhesion and hydrophilicity of polymer surfaces, focused on industrial materials processing rather than environmental plastic pollution.
Changes in the Chemical Composition of Polyethylene Terephthalate under UV Radiation in Various Environmental Conditions.
Researchers exposed polyethylene terephthalate (PET) to UV radiation under controlled humidity conditions and tracked changes in its chemical composition, finding progressive oxidation and chain scission that alter the polymer's surface properties. Understanding how PET degrades under UV exposure is important for predicting how PET microplastics form and what chemical changes make them more or less bioavailable.
Changes in the Chemical Composition of Polyethylene Terephthalate Under UV Radiation in Various Environmental Conditions.
Researchers studied how UV radiation degrades PET plastic under varying humidity (dry vs. saturated) and temperature (30-50 degrees C) conditions for up to 20 days. High humidity and elevated temperature significantly accelerated ester bond cleavage and carboxylic acid formation, key chemical changes that produce micro-nano plastics.
The proliferation and colonization of functional bacteria on amorphous polyethylene terephthalate: Key role of ultraviolet irradiation and nonionic surfactant polysorbate 80 addition
Researchers showed for the first time that UV irradiation and the surfactant Tween-80 act synergistically to promote bacterial colonization of amorphous PET plastic: UV creates surface attachment sites while Tween-80 boosts bacterial proliferation and surface hydrophobicity, together setting the stage for subsequent biodegradation.
Rheological Characterization of UV and Shear‐Induced Degradation of Poly(Ethylene Terephthalate): Linking Environmental and Processing Histories to Recyclability
Researchers studied how UV light exposure and mechanical processing degrade PET plastic at the molecular level. They found that UV aging in water environments causes the plastic chains to break apart, while dry conditions promote crosslinking, and that even a single round of recycling processing dramatically reduces crystal size and releases volatile byproducts. The study reveals that both environmental weathering and recycling significantly weaken PET's mechanical properties, which has implications for both microplastic generation and plastic recyclability.