Studying the Degradation of Three Polymers under Different Chlorine Concentrations and Exposure Times
Summary
Researchers studied the degradation of PVC, high-density polyethylene, and polypropylene when exposed to chlorine solutions used in swimming pools and water treatment plants. The study found that the degree of material wear depended on both chlorine concentration and exposure time, with different polymers showing varying susceptibility to chlorine-induced degradation.
Due to chlorine's ability to kill bacteria and fungi through a chemical reaction, chlorine solutions are commonly used to clean and disinfect numerous public facilities, although these actions are also dependent to the equipment present in those facilities. Accordingly, the interest in studying its effect when in contact with different materials is obvious. This study was carried out through accelerated degradation tests and various analysis methods (optical microscope, scanning electron microscope, and tensile tests). The objective was to observe the wear presented by three polymeric materials, polyvinyl chloride (PVC), high-density polyethylene (HDPE), and polypropylene (PP), when exposed to chlorine's action in swimming pools and drinking water treatment plants. The resulting effect depends on the chlorine content and the type of contact between the chemical agent and the material. The aim was to select the material less likely to be affected by chlorine through tests and analyses, allowing a longer component life. The use of certain more resistant polymeric materials can drastically reduce maintenance, reducing fundamental factors such as costs, the downtime of municipal facilities, and also the risk to public health. It was concluded that PVC has the most stable behaviour overall when in contact with chlorine solutions.
Sign in to start a discussion.
More Papers Like This
The Impact of Chlorinated Water and Sun Exposure on the Durability and Performance of Swimwear Materials
Researchers studied how chlorinated pool water and sun exposure degrade swimwear materials made from blends of polyamide, polyester, and elastane. They found that these aging conditions caused significant deterioration of the fabrics' mechanical properties and durability over time. The findings are relevant to microplastic pollution because degrading swimwear releases synthetic fibers into pool and natural water environments.
Behavior of Polymer Materials Exposed to Aging in the Swimming Pool: Focus on Properties That Assure Comfort and Durability
Researchers aged polyamide and polyester polymers used in swimming pool equipment under pool-water conditions and found that both materials underwent molecular-level degradation that reduced comfort-related properties, with implications for microplastic release into pool water.
Chemical and physical changes of microplastics during sterilization by chlorination
Researchers exposed common plastic types to chlorination conditions used in water and wastewater treatment and measured the resulting chemical and physical changes. They found that polystyrene was most susceptible to degradation from chlorine exposure, while polypropylene was most resistant. The study suggests that wastewater chlorination may alter the surface properties of microplastics, potentially affecting how they interact with contaminants and organisms in the environment.
Volatile organic compounds generation pathways and mechanisms from microplastics in water: Ultraviolet, chlorine and ultraviolet/chlorine disinfection
Researchers examined how UV, chlorine, and combined UV/chlorine disinfection treatments cause microplastics to release volatile organic compounds, identifying distinct degradation pathways for polypropylene, polystyrene, and PVC that generate diverse chemical byproducts in treated water.
Disinfection impacts: Effects of different disinfection treatments on common polymer types to guide the identification of polymers of concern in the water industry
Researchers tested how common water disinfection methods, including chlorination and chloramination, affect seven types of plastic particles at different doses and pH levels. They found that both treatments caused measurable physical and chemical changes to the polymers, with some plastics showing significant surface degradation and chemical alterations. The findings suggest that water treatment processes may unintentionally transform microplastics in ways that could affect their environmental behavior and potential health impacts.