Aging Process of Biocomposites with the PLA Matrix Modified with Different Types of Cellulose
Summary
Researchers prepared polylactic acid composites with three different cellulose-based fillers and studied how they age under UV light exposure. The study found that the type of cellulose additive plays a crucial role in how well the material resists UV degradation, with some forms improving both mechanical properties and degradation timing. These findings support the potential of biodegradable polymer composites as alternatives to conventional plastics that generate persistent microplastic waste.
In the modern world, many products are disposable or have a very short lifespan, while at the same time, those products are made from materials that will remain in the environment in the form of waste for hundreds or even thousands of years. It is a serious problem; non-biodegradable polymer wastes are part of environmental pollution and generate microplastics, which accumulate in the organisms of living beings. One of the proposed solutions is biodegradable polymers and their composites. In our work, three types of polylactide-based composites with plant-derived fillers: microcellulose powder, short flax fibers, and wood flour at 2 wt.% were prepared. Poly(lactic acid) (PLA)-based biocomposite properties were characterized in terms of mechanical and surface properties together with microscopic analysis and Fourier-transform infrared spectroscopy (FTIR), before and after a UV (ultraviolet)-light-aging process to determine the effects of each cellulose-based additive on the UV-induced degradation process. This research shows that the addition of a cellulose additive can improve the properties of the material in terms of the UV-aging process, but the form of the chosen cellulose form plays a crucial role in this case. The testing of physicochemical properties demonstrated that not only can mechanical properties be improved, but also the time of degradation under UV light exposure can be controlled by the proper selection of the reinforcing phase and the parameters of the extrusion and injection molding process. The obtained results turned out to be very interesting, not only in terms of the cost reduction of the biocomposites themselves, as mainly the waste from the wood industry was used as a low-cost filler, but also that the additive delays the aging process occurring during UV light exposure. Even a small, 2 wt.% addition of some of the tested forms of cellulose delayed surface degradation, which is one of the most important factors affecting the biodegradation process.
Sign in to start a discussion.
More Papers Like This
Aging of PLA/NR electrospun fibers under the influence of UV-irradiation, water and soil environment
Researchers tested how UV light, water, and soil exposure age and degrade biodegradable polylactic acid (PLA) and natural rubber (NR) composite fibers. Higher natural rubber content accelerated degradation, important information for designing biodegradable plastic products that break down as intended without generating persistent microplastics.
Environmental Degradation of Plastic Composites with Natural Fillers—A Review
Researchers examined the environmental degradation of polymer composites containing natural fillers, finding that exposure to outdoor conditions accelerates biodegradation of natural components and alters the mechanical properties of the composite material. The degradation process can generate microplastic fragments as the matrix breaks down.
Mechanical properties of fibre/ filler based poly(Lactic Acid) (Pla) composites : A brief review
This review examines the mechanical properties of polylactic acid (PLA)-based composites reinforced with natural fibers and fillers, presenting PLA as a biodegradable alternative to conventional plastics in applications ranging from agriculture to biomedical devices. Improving the strength and durability of bio-based plastics is essential for replacing petroleum-based materials that generate persistent microplastic pollution.
Comparing the Aging Processes of PLA and PE: The Impact of UV Irradiation and Water
Scientists compared how biodegradable PLA plastic and conventional polyethylene break down under UV light and water exposure. PLA degraded more severely, fragmenting into smaller particles more readily than polyethylene, though both types developed surface cracks and chemical changes. Understanding how different plastics age is important because smaller, more degraded particles may be more easily absorbed by living organisms and potentially cause greater harm.
Degradation of Biodegradable Microplastics under Artificially Controlled Aging Conditions with UV Radiation
Researchers subjected biodegradable plastics to controlled UV aging and found that they fragmented into microplastics faster than conventional plastics under simulated outdoor conditions. Biodegradable plastics are promoted as an eco-friendly alternative, but this study shows they may actually create microplastic pollution more rapidly in real-world environments. The findings raise important questions about whether biodegradable plastics are a genuine solution to plastic pollution.