Microplastic-Related Leachate from Recycled Rubber Tiles: The Role of TiO2 Protective Coating
AI summary Read the abstract
Researchers tested whether coating recycled rubber tiles with titanium dioxide could reduce the environmental impact of microplastic-related chemical leaching. They found that the TiO2 coating helped stabilize polymer degradation and reduced leaching of some organic compounds like phthalates after UV aging. However, the coating also increased wear particle generation, suggesting a trade-off between chemical protection and physical abrasion in recycled rubber products.
The extensive global use of rubber results in significant microplastic pollution from the release of tire wear particles and microplastic leachate, impacting the environment, human health, and ecosystems. Waste tires are normally recycled and used for the production of new products, such as rubber tiles. The presented study aims to show the possibility of further decrease in the negative environmental impact of materials based on recycled rubber. This paper presents the modification of rubber tiles with a titanium dioxide (TiO2) coating, focusing on surface integrity, rubber particle wear release, and the consequent environmental impact of leachate release. Both reference and modified rubber tiles were subjected to artificial accelerated aging in a solar simulator for 4, 6, and 8 weeks, followed by an abrasion test. The carbonyl index was calculated from FTIR characterization after each time frame to indicate the degradation of organic compounds and chemical changes caused by UV exposure. A 24 h leaching test with a liquid-to-sample ratio of 1:20 was performed on both rubber tile samples prior to and after 8 weeks of aging along with the aged wear particles for the purpose of the non-target screening of released organic leachate by LC/MS QTOF. The results of carbonyl indices showed that the TiO2 coating contributes to the stabilization of polymer degradation and, to a certain extent, reduces the leaching of organic compounds, such as phthalates. However, the increased wear and release of rubber particles and the subsequent degradation of organic leachates require further in-depth research.
More Papers Like This
Weathering alters surface characteristic of TiO2-pigmented microplastics and particle size distribution of TiO2 released into water
AI summary Read the abstract
Researchers systematically investigated how UV weathering affects surface properties of TiO2-pigmented microplastics and the size distribution of TiO2 particles released into water. Aged microplastics released more TiO2 particles faster than unaged ones, with a greater proportion of large particles (>5 micrometers), as photo-oxidation increased carbonyl content, caused surface cracking, and altered the fragility and leaching behavior of the plastic.
Contaminant release from aged microplastic
AI summary Read the abstract
Researchers exposed recycled plastic granules of polyethylene, PVC, and polystyrene to simulated aging conditions including UV radiation and high temperatures. They found that aging significantly increased the rate at which chemical additives leached from the plastic particles into water, with UV exposure having the greatest effect. The study highlights that weathered microplastics in the environment may release harmful chemicals at much higher rates than fresh plastic materials.
UV and thermal degradation of tire derivatives: A comparative study of unused tires, recycled tire chips, and tire and road wear particles
AI summary Read the abstract
Researchers compared UV and thermal aging behavior of unused tires, recycled tire chips, and tire and road wear particles, finding that material history and particle size influenced degradation rate and benzothiazole leaching—a marker of toxicological concern from tire-derived microplastics.
Influence of chemical aging processes on releasing organic products from microplastics
AI summary Read the abstract
This study examined how chemical aging processes, including UV exposure and oxidation, affect the release of organic compounds from microplastic particles. The results showed that weathered microplastics release different and sometimes more abundant chemical products than pristine particles, increasing their chemical hazard in the environment.
Weathering alters the profile of trace metals and organic compounds in leachates and bioavailability extracts from microplastics of trail running shoes
AI summary Read the abstract
Trail running shoes shed rubber microplastics that, when weathered on soil surfaces under UV exposure, release zinc, sulfur, titanium, and fatty acids into the environment at increasing rates over time. However, weathering also reduces the bioaccessibility of some toxic organic additives, while producing new transformation byproducts. The study underscores that the toxicity profile of tire and shoe rubber microplastics changes substantially as they age in the environment, and that ecotoxicology studies should use weathered rather than pristine particles to accurately reflect real-world risks.