Transformation Microstructure and Delayed Fracture Characteristics of Medium-Carbon (0.25C) Ni-Cr-Mo-V Steel

강찬형; 맹선재

0

Article ? AI-assigned paper type based on the abstract. Classification may not be perfect — flag errors using the feedback button. Tier 2 ? Original research — experimental, observational, or case-control study. Direct primary evidence. Food & Water Sign in to save

Transformation Microstructure and Delayed Fracture Characteristics of Medium-Carbon (0.25C) Ni-Cr-Mo-V Steel

Original title: 중탄소 ( 0.25C ) Ni - Cr - Mo - V 강의 변태조직과 지연파괴특성 (遲延破壞特性)

대한금속재료학회지 1980

강찬형, 맹선재

Summary

This Korean-language study investigated the relationship between microstructure (martensite, lower bainite, and mixed 1:1 ratio) and delayed fracture behavior of 0.25C-Ni-Cr-Mo-V steel tempered to the same tensile strength level. Results showed that lower bainite microstructure had the highest resistance to delayed fracture as measured by K_ISCC values.

0.25C-2.5Ni-2.5Cr-0.5Mo-0.1V鋼의 變態組織과 遲延破壞擧動 사이의 關係를 調査하였다. 즉 Martensite 組織, lower bainite 組織 및 이들의 1對 1 比率의 混合組織을 만들어 同一한 引張强度水準(143㎏/㎟)이 되도록 tempering (450℃,40分) 시킨 後 25℃의 蒸溜水雰圍氣 속에서 외팔보 굽힘試驗機로 遲延破壞試驗을 實施하였다. K_(ISCC) 값으로 評價할 때 lower bainite 組織이 가장 優秀하였고 martensite 組織은 이보다 약간 低下하였으며 混合組織에서 가장 낮은 값을 나타내었다. Martensite 組織과 混合組織의 破面樣相은 모두 粒界破面이었다. 그러나 martensite組織에서는 粒界에 ductile tearing의 量이 顯著히 많았다. Lower bainite 組織의 破面은 microplastic tearing과 microvoid coalescence가 混在한 樣相이다. 위 實驗結果들을 Oriani의 水素脆性에 관한 decohesion說과 關聯시켜 論議하였다. 특히 混合組織의 遲延破壞特性이 單一組織의 경우보다 낮은 것은 martensite와 lower bainite의 境界面에서 水素에 依한 decohesion이 促進된 때문이라고 說明된다.