Mechanics of microwear traces in tooth enamel
Summary
Researchers modeled microwear traces in tooth enamel using indentation mechanics, showing that pits and scratches are produced at forces well below normal biting loads and that the transition from mild plastic deformation to microcracking depends on particulate sharpness and angularity in food — with particular relevance to diet evolution in hominins.
It is hypothesized that microwear traces in natural tooth enamel can be simulated and quantified using microindentation mechanics. Microcontacts associated with particulates in the oral wear medium are modeled as sharp indenters with fixed semi-apical angle. Distinction is made between markings from static contacts (pits) and translational contacts (scratches). Relations for the forces required to produce contacts of given dimensions are derived, with particle angularity and compliance specifically taken into account so as to distinguish between different abrasives in food sources. Images of patterns made on human enamel with sharp indenters in axial and sliding loading are correlated with theoretical predictions. Special attention is given to threshold conditions for transition from a microplasticity to a microcracking mode, corresponding to mild and severe wear domains. It is demonstrated that the typical microwear trace is generated at loads on the order of 1N - i.e. much less than the forces exerted in normal biting - attesting to the susceptibility of teeth to wear in everyday mastication, especially in diets with sharp, hard and large inclusive intrinsic or extraneous particulates.
Sign in to start a discussion.
More Papers Like This
A model for predicting wear rates in tooth enamel
Researchers developed a theoretical model for predicting tooth enamel wear rates based on the mechanics of micro-scale contact events with sharp particles, validating it against experimental data and showing that sharp, hard particulates in food — rather than overall bite force — govern the transition between mild and severe enamel wear.
Contact damage of human dental enamel under cyclic axial loading with abrasive particles
Researchers investigated how cyclic axial loading in a silica particle medium damages human dental enamel at multiple scales, finding that while macroscopic wear is negligible, abrasive particles cause surface microindentation and subsurface demineralization that can degrade fracture strength over time.
Wear of ceramic-based dental materials
Researchers compared wear rates and failure mechanisms of several ceramic-based dental materials using a laboratory test simulating chewing contact, finding that zirconia showed the lowest wear and lithium disilicate the highest, with microcracking and microplasticity (small-scale plastic deformation) identified as the key material-removal mechanisms.
Biomechanics of Teeth Alignment Using Clear Aligners with Various Attachment Shapes and Orientations
Researchers studied the biomechanics of teeth alignment using clear aligners with various attachment shapes and orientations. The study examines how these thermoformed or 3D-printed plastic appliances apply biomechanical forces to trigger tooth movement, relevant to understanding microplastic release from dental devices during orthodontic treatment.
Atomistic Studies of Nanoindentation—A Review of Recent Advances
This review covers advances in using computer simulations to understand how materials deform at the nanoscale during nanoindentation testing. The research is in materials science and not directly related to environmental microplastics.