Photo-Oxidative Degradation Mitigated the Developmental Toxicity of Polyamide Microplastics to Zebrafish Larvae by Modulating Macrophage-Triggered Proinflammatory Responses and Apoptosis
Summary
Visible light photo-oxidation of polyamide microplastics for 90 days reduced particle size, generated nanoparticles, and significantly mitigated developmental toxicity in zebrafish larvae by modulating macrophage-triggered inflammatory responses and apoptosis — suggesting weathering can reduce but not eliminate MP toxicity.
Microplastics (MPs) are ubiquitous in the environment and pose substantial threats to the water ecosystem. However, the impact of natural aging of MPs on their toxicity has rarely been considered. This study found that visible light irradiation with hydrogen peroxide at environmentally relevant concentration for 90 days significantly altered the physicochemical properties and mitigated the toxicity of polyamide (PA) fragments to infantile zebrafish. The size of PA particles was reduced from ∼8.13 to ∼6.37 μm, and nanoparticles were produced with a maximum yield of 5.03%. The end amino groups were volatilized, and abundant oxygen-containing groups (e.g., hydroxyl and carboxyl) and carbon-centered free radicals were generated, improving the hydrophilicity and colloidal stability of degraded MPs. Compared with pristine PA, the depuration of degraded MPs mediated by multixenobiotics resistance was much quicker, leading to markedly lower bioaccumulation in fish and weaker inhibition on musculoskeletal development. By integrating transcriptomics and transgenic zebrafish [Tg(lyz:EGFP)] tests, differences in macrophages-triggered proinflammatory effects, apoptosis via IL-17 signaling pathway, and antioxidant damages were identified as the underlying mechanisms for the attenuated toxicity of degraded MPs. This work highlights the importance of natural degradation on the toxicity of MPs, which has great implications for risk assessment of MPs.
Sign in to start a discussion.
More Papers Like This
Photoaging enhanced the adverse effects of polyamide microplastics on the growth, intestinal health, and lipid absorption in developing zebrafish
Researchers found that polyamide microplastics became significantly more harmful to developing zebrafish after being aged by simulated sunlight, shrinking in size and generating nanoplastic fragments. The aged particles caused greater damage to intestinal health, impaired lipid absorption, and stunted growth compared to unaged microplastics. The study demonstrates that environmental weathering can substantially increase the biological risks posed by microplastics in aquatic ecosystems.
Photolytic degradation elevated the toxicity of polylactic acid microplastics to developing zebrafish by triggering mitochondrial dysfunction and apoptosis
Researchers found that biodegradable polylactic acid (PLA) microplastics become more toxic to zebrafish after being broken down by sunlight over 90 days. UV exposure shrank the particles and generated nanoplastics, which were harder for the fish to expel from their bodies compared to the original material. The degraded PLA triggered oxidative stress and mitochondrial damage in developing zebrafish, suggesting that the environmental breakdown of biodegradable plastics may actually increase their harmful effects.
Photoaged microplastics induce neurotoxicity via oxidative stress and abnormal neurotransmission in zebrafish larvae (Danio rerio)
This study found that microplastics aged by sunlight were more toxic to zebrafish larvae than fresh microplastics, causing brain damage and abnormal behavior. The sun-aged particles triggered greater oxidative stress and disrupted neurotransmitter systems in the developing fish. This is concerning because most microplastics in the environment have been weathered by sunlight, meaning the real-world health risks may be greater than lab studies using fresh plastics suggest.
Aged polystyrene microplastics exposure affects apoptosis via inducing mitochondrial dysfunction and oxidative stress in early life of zebrafish
Zebrafish embryos exposed to UV-aged polystyrene microplastics at environmental concentrations showed more severe developmental problems than those exposed to fresh microplastics. The aged particles caused greater oxidative stress and mitochondrial damage, triggering increased cell death during early development -- suggesting that weathered microplastics in the real environment may be more harmful than the pristine particles typically used in lab studies.
Progress on the photo aging mechanism of microplastics and related impact factors in water environment
This review examined the photo-aging mechanisms of microplastics in aquatic environments, finding that solar UV radiation drives oxidation reactions that alter surface chemistry, fragment particles further, and enhance their capacity to adsorb and release co-occurring pollutants.