Cellulose nanofibers/polyvinyl alcohol blends as an efficient coating to improve the hydrophobic and oleophobic properties of paper
Summary
Researchers developed a paper coating made from cellulose nanofibers and polyvinyl alcohol and found it significantly improved paper's resistance to both water and grease while also increasing tensile strength, offering a potentially more sustainable alternative to the plastic-based coatings currently used in food packaging.
The effect of cellulose nanofibers (CNFs)/polyvinyl alcohol (PVA) coating on the hydrophobic, oleophobic, and strength properties of paper were investigated. The results showed that the size of bamboo fibers (BFs) decreased significantly and the crystallinity increased significantly after biological enzyme treatment. The average length of CNFs obtained by high pressure homogenization was 2.4 µm, the diameter was 28.7 nm, and the crystallinity was 63.63%. When the coating weight of PVA/CNF was 2.0 g/m2 and the CNF dosage was increased from 0.0% to 3.0%, the paper grease resistance grade was increased from 7 to 9, the Cobb value was decreased from 22.68 ± 0.29 g/m2 to 18.37 ± 0.63 g/m2, the contact angle was increased from 67.82° to 93.56°, and the longitudinal and transverse tensile index were increased from 67.72 ± 0.21 N m/g and 37.63 ± 0.25 N m/g to 68.61 ± 0.55 N m/g and 40.71 ± 0.78 N m/g, respectively. When the CNF dosage was 3.0% and the coating weight of PVA/CNF was 4.0 g/m2, the grease resistance grade of the paper was 12, the Cobb value was 21.80 ± 0.39 g/m2, and the longitudinal and transverse tensile indices were 72.11 ± 0.43 N m/g and 42.58 ± 0.48 N m/g, respectively. In summary, the increase of CNFs can effectively improve the lipophobicity, hydrophobicity and tensile strength of the PVA coated paper.
Sign in to start a discussion.
More Papers Like This
Oil‐ and water‐resistant paper substrate using blends of chitosan‐graft‐polydimethylsiloxane and poly(vinyl alcohol)
Researchers developed a plastic- and fluorine-free coating approach for oil and water repellent paper substrates using blends of poly(vinyl alcohol) and chitosan-graft-polydimethylsiloxane copolymer, offering an economical alternative to conventional coatings that contribute to microplastic contamination.
Bio-Based Monoepoxy-TerminatedPolysiloxane-ModifiedCoating for Hydrophobic and Oil-Resistant Paper
Researchers developed a bio-based coating material by grafting monoepoxy-terminated polysiloxane onto chitosan and cellulose nanofibers via a one-pot method, producing films with tunable hydrophobic and oil-resistant properties for sustainable packaging paper as an alternative to nondegradable plastic coatings.
Cellulose nanofibrils and silver nanoparticles enhances the mechanical and antimicrobial properties of polyvinyl alcohol nanocomposite film
Researchers developed a biodegradable polyvinyl alcohol nanocomposite film reinforced with sugarcane bagasse cellulose nanofibrils and silver nanoparticles, finding that the combination significantly improved mechanical strength and antimicrobial properties, offering a sustainable alternative to conventional plastic food packaging.
Boric acid-crosslinked poly(vinyl alcohol): biodegradable, biocompatible, robust, and high-barrier paper coating
Researchers developed a paper coating using polyvinyl alcohol crosslinked with boric acid that significantly improves the paper's barrier properties and mechanical strength. The study found that this coating remains fully biodegradable and biocompatible despite its enhanced performance. The findings suggest a practical, environmentally friendly alternative to traditional plastic-based packaging coatings.
Preparation and Characterization of Degradable Cellulose−Based Paper with Superhydrophobic, Antibacterial, and Barrier Properties for Food Packaging
Researchers prepared food packaging paper coated with polylactic acid and cinnamaldehyde as a barrier layer and nano silica-modified stearic acid as a superhydrophobic outer layer, creating a cellulose-based alternative to plastic packaging. The resulting material showed excellent water resistance, thermal stability, and antimicrobial activity while being made from renewable and biodegradable components.