Influence of Different Environments and Temperatures on the Photo-Oxidation Behaviour of the Polypropylene
AI summary Read the abstract
Researchers investigated the photo-oxidation behavior of polypropylene under irradiation in air, distilled water, and seawater at two temperatures, finding that oxidation was dramatically faster in air than in aqueous media due to limited oxygen availability, with degradation rates increasing with temperature in all environments.
The photo-oxidation of polypropylene at two different temperatures and in three different environments-air, distilled water and sea water-has been followed as a function of the irradiation time. The photo-oxidation kinetic is dramatically dependent on the amount of oxygen available for the oxidation reactions and on the temperature. While the photo-oxidation is very fast in air, the degradation is much slower in the two aqueous media. The degradation in sea water is slightly slower than in distilled water. In all cases, the degradation kinetic increases remarkably with the temperature. This behavior has been attributed to the lower oxygen availability for the oxidation reactions of the polymers. The light difference of the degradation kinetic between the two aqueous media depends on the small difference of the oxygen concentration at the test temperatures of 40 and 70 °C. At the latter temperature, the difference between the degradation kinetic in distilled water and sea water is still less important because increasing the temperature decreases the solubility of the oxygen, and it tends to became very similar in both samples of water.
More Papers Like This
Accelerated degradation of low-density polyethylene in air and in sea water
AI summary Read the abstract
UV-accelerated weathering of low-density polyethylene in air and floating in seawater was compared using FTIR depth profiling, finding that oxidation was diffusion-controlled in both media and localized to a thin surface layer, but that seawater slowed the overall degradation rate.
Degradation of polypropylene : proportion of microplastics formed and assessment of their density.
AI summary Read the abstract
Researchers quantified the proportion of microplastics generated during UV-driven degradation of polypropylene and assessed changes in chemical composition caused by photooxidation. The study found that UV exposure progressively fragments polypropylene and alters its surface chemistry, affecting subsequent environmental behavior and toxicity.
Characterising the deterioration of different plastics in air and seawater
AI summary Read the abstract
Four plastic types were exposed in air and seawater under light and shade conditions for up to 600 days, finding that deterioration (loss of extensibility and increasing oxidation) was faster in air than in seawater and accelerated by direct sunlight. The results indicate that plastics entering marine environments degrade more slowly than land-based plastics, with important implications for the timescale of microplastic generation.
Photo aging and fragmentation of polypropylene food packaging materials in artificial seawater
AI summary Read the abstract
Photo-aging and fragmentation of two common polypropylene (PP) food packaging materials with different additive contents were studied under artificial accelerated weathering. Additive composition significantly influenced the rate of photochemical aging and fragmentation into microplastic particles, with implications for how packaging design affects microplastic generation in the marine environment.
Influence of UV exposure time and simulated marine environment on different microplastic degradation
AI summary Read the abstract
Researchers examined how UV radiation and saltwater conditions affect the degradation of polypropylene, polystyrene, and ethylene-vinyl acetate microplastics. The study found that each polymer type responded differently to photodegradation, with changes in surface properties, crystallinity, and chemical bond formation varying by material. Evidence indicates that saline marine conditions can intensify certain degradation processes, suggesting that multiple environmental factors must be considered when assessing microplastic breakdown.