Insight into Degrading Effects of Two Fungi on Polyurethane Coating Failure in a Simulated Atmospheric Environment
AI summary Read the abstract
Researchers found that two fungi collected from an atmospheric corrosion site — Talaromyces funiculosus and Phanerochaete chrysosporium — caused measurable biodegradation of polyurethane coatings under high humidity conditions, revealing biological pathways for polymer coating failure.
Two different fungi, Talaromyces funiculosus (T. funiculosus) and Phanerochaete chrysosporium (P. chrysosporium), were collected from the Xishuangbanna atmospheric corrosion site and incubated on a polyurethane (PU) coating at 30 °C for two weeks under 95% relative humidity (RH). The biodegrading effects of these fungi on the coating failure were investigated from aspects of metabolism and electrochemistry. The results showed that T. funiculosus contributed more to the degradation of the PU coating failure than P. chrysosporium, and two factors played dominant roles. First, the weight of the T. funiculosus mycelium was nearly 3 times more than that of P. chrysosporium, indicating there was more substrate mycelium of T. funiculosus deep into the coatings to get more nutrition in atmospheric during colonization. Second, T. funiculosus secreted carboxylic acids, such as citric, propanoic, succinic, and tartaric acids, and accelerated the hydrolysis of the ester and urethane bonds in the PU coatings. As a result, the mycelium of T. funiculosus readily penetrated the interface of the coating and substrate resulting in a rapid proliferation. Thus, the |Z|0.01Hz value of the coating decreased to 5.1 × 104 Ω·cm2 after 14 days of colonization by T. funiculosus while the value remained at 7.2 × 107 Ω·cm2 after colonization by P. chrysosporium. These insights suggest that the biodegradation process in simulated atmospheric environments would provide theoretical guidance and directions for the design of antifungal PU coatings.
More Papers Like This
Edge-Localized Biodeterioration and Secondary Microplastic Formation by Papiliotrema laurentii Unsaturated Biofilm Cells on Polyurethane Films
AI summary Read the abstract
A yeast species was found to preferentially degrade the ester bonds at the edges of polyurethane coatings, producing secondary microplastic particles. This mechanism of microplastic generation from painted surfaces suggests that building coatings and infrastructure are an underappreciated source of plastic pollution.
Fungal microbiota of biodamages of various polymeric materials
AI summary Read the abstract
Researchers catalogued the dominant fungal genera colonizing synthetic polymers — including materials used in aerospace — and demonstrated that Aspergillus fumigatus, Penicillium chrysogenum, and related species degrade polyethylene and PET, then assembled optimized fungal test kits with fewer strains that outperform older standard kits for evaluating polymer biostability.
Ability of fungi isolated from plastic debris floating in the shoreline of a lake to degrade plastics
AI summary Read the abstract
Researchers isolated over 100 fungal strains from plastic debris floating in a Swiss lake and tested their ability to degrade polyethylene and polyurethane, finding that none could degrade polyethylene but four species degraded polyurethane. The results highlight the limited capacity of naturally occurring plastic-colonizing fungi to break down the most abundant plastic polymers in the environment.
Solving the plastic dilemma: the fungal and bacterial biodegradability of polyurethanes
AI summary Read the abstract
This review examined the biodegradability of polyurethane by fungi and bacteria, identifying promising microbial species and enzymes capable of breaking down this widely used but environmentally persistent plastic polymer.
Understanding visible light and microbe-driven degradation mechanisms of polyurethane plastics: Pathways, property changes, and product analysis
AI summary Read the abstract
Researchers found that polyurethane plastics break down in water through a combination of microbial action and light exposure, producing secondary microplastics as they degrade. This study reveals a previously underappreciated source of microplastic pollution, since polyurethane is widely used in coatings, foams, and other products that often end up in waterways.