Microplastic formation and simultaneous release of phthalic acid esters from residual mulch film in soil through mechanical abrasion

The application of plastic mulch film could effectively enhance the productivity of facility agriculture. However, releasing microplastic and phthalate from mulch films in soil has attracted increasing concerns, and releasing characters of microplastic and phthalate from mulch films during their mechanical abrasion remains unclear. This study elucidated the dynamics and impact factors of microplastic generation, including the thickness, polymer types and ageing of mulch film during mechanical abrasion. Releasing characters of the di(2-Ethylhexyl) phthalate (DEHP), a common type of phthalate in soil, from mulch film during mechanical abrasion were also explored. Results showed that 2 pieces of mulch film debris increased to 1291 pieces of microplastic after five days of mechanical abrasion, with exponential growth in the microplastic generation. After mechanical abrasion, the thinnest (0.008 mm) mulch film completely transformed into microplastics. However, the thicker mulch (>0.01 mm) suffered slight disintegration, making it feasible to be recycled. The biodegradable mulch film discharged the most microplastics (906 pieces) compared with the HDPE (359 pieces) and LDPE (703 pieces) mulch film after three days of mechanical abrasion. In addition, the mild thermal and oxidative ageing could result in 3047 and 4532 pieces of microplastic emissions from mulch film after three days of mechanical abrasion, which were ten times more than the original mulch film (359 pieces). Furthermore, negligible DEHP was released from mulch film without mechanical abrasion, while the released DEHP significantly correlated with generated microplastics during mechanical abrasion. These results demonstrated the crucial role of mulch film disintegration in phthalate emissions.