Production and characterization of human hair keratin bioplastic films with novel plasticizers

Since their invention, conventional plastics have contributed in the betterment of the society in numerous ways, nevertheless their deleterious impacts on the natural ecosystems and living creatures is irrefutable. The management of plastic waste generated is a concern worldwide and therefore quest for the plastic alternates or bioplastics is imminent. Here, we explore the suitability of keratin from human hair waste as the candidate for the production of bioplastic films. Keratin extracted from hair was used to form the films or 'kertics' by solution casting and curing. Ethanediol, di-ethylene glycol and tri-ethylene glycol were used as novel plasticizers along with glycerol in the keratin film formation. The film prepared were of the thickness 190-220 µm with the area of about 4.54 ± 0.2 cm2. Water uptake by G100, ED100, DEG100 and TEG100 films was recorded to be 4.8, 6.2, 4.9 and 6.3% respectively. FESEM analysis revealed that the films with 100 µl of 1% glycerol (G100) had continuous surface morphology except few pits of 0.1 µm, also DEG100 and TEG100 films have the most uniform surface morphology with no evident pits, holes or bulges. X-ray diffractogram showed characteristic peak of keratin at 19.5° and the d-spacing value observed was 0.45 nm. The FTIR studies suggested that the films retained keratin in non degraded form, and possessed the characteristic Amide peaks. The films were also found to be biodegradable in studies involving keratinophilic fungal strain of A. oryzae. These films could found potential applications in packaging industry, disposable items manufacturing and biomaterial generation.