Effect of Cooling Rate on Microstructure Evolution and Mechanical Properties of SCM435 Steel
Summary
Researchers investigated how cooling rate affects microstructure evolution and mechanical properties of SCM435 cold heading steel using scanning electron microscopy, TEM, XRD, and electron backscatter diffraction. Results showed that cooling rate significantly determines the phase composition, grain structure, and resulting strength and ductility of the steel.
The microstructural evolution of SCM435 cold heading steel at different cooling rates was investigated by means of scanning electron microscopy, TEM, XRD, and electron backscatter diffraction. The results show that the cooling rate has a significant effect on the microstructure of the experimental steel. With an acceleration in the cooling, the microstructure of the steel gradually changed from ferrite and pearlite to ferrite, pearlite, and granular bainite; finally, the pearlite disappeared, and the microstructure changed to acicular ferrite, bainite, and martensite. With an increase in the cooling rate, the morphology of the carbide underwent an evolution from sheet carbide to short-rod carbide, granular carbide, and ultimately thin-strip carbide. With the acceleration in cooling, the proportion of large-angle grain boundaries gradually decreased, and the area of small-angle grain boundaries gradually increased. When the cooling rate was 0.1 °C/s, the proportion of large-angle grain boundaries was as high as 52.8%, and the dislocation density was only 1.91 × 1012 cm−2. When the cooling rate was 2.0 °C/s, the proportion of large-angle grain boundaries was only 27.1%, and the dislocation density increased to 5.38 × 1012 cm−2. With the increase in the cooling rate, the depth of the decarbonization layer and the thickness of the scale oxide gradually decreased, the proportion of the FeO phase in the scale phase gradually decreased, and the proportion of the Fe3O4 phase and Fe2O3 phase gradually increased. The tensile strength increased monotonously with the increase in cooling rate, whereas the elongation and area reduction first decreased, then increased, and then decreased. When the cooling rate was 1.0 m/s, the short rod and granular bainite in the material structure endowed the SCM435 steel with excellent strength and toughness matching, and the tensile strength and elongation of the steel reached 895 MPa and 24%, respectively.
Sign in to start a discussion.
More Papers Like This
Effect of Cooling Rate on Microstructure Evolution and Mechanical Properties of SCM435 Steel
This materials science study examined how cooling rates during steel production affect the microstructure and mechanical properties of SCM435 steel. This metallurgy paper has no connection to microplastics or environmental health.
Effect of heat treatment on microstructure and properties of 10B21 cold-heading steel for fasteners
This metallurgy study examined how different heat treatment processes affect the microstructure and mechanical properties of 10B21 boron steel used to manufacture fasteners. Converting the microstructure from ferrite to tempered martensite through quenching and tempering improved strength and hardness.
Dynamic Processes of Substructural Rearrangement under Friction of Carbon Steel
This study examined how heat treatment affects the friction and wear properties of medium carbon steel, linking material microstructure to tribological performance. The research is focused on materials engineering with limited direct relevance to microplastic pollution or human health.
Quantification and effects of microstructural dispersions on the mechanical behaviour of low carbon martensite
Researchers examined the mechanical behaviour of low-carbon martensitic steel, demonstrating that the sequential nature of the martensitic phase transformation from the Ms temperature to ambient temperature produces microstructural heterogeneities rather than a uniform phase. This reinterpretation — viewing lath martensite as a multiphase aggregate — helps explain paradoxical properties such as low microplasticity yield and strong initial hardening.
Research on Formability of 304 Stainless Steel Foil Micro-Deep Drawing
This study investigated how heat treatment and microstructure affect the formability of ultra-thin 304 stainless steel foil in micro-deep drawing processes used to manufacture miniature components. The results show that annealing temperature significantly influences grain structure and forming performance, with implications for precision manufacturing.