Effect of Copper Antifouling Paint on Marine Degradation of Polypropylene: Uneven Distribution of Microdebris between Nagasaki Port and Goto Island, Japan
AI summary Read the abstract
Researchers characterised marine microdebris including microplastics and copper-based paint particles collected at five stations between Nagasaki Port and Goto Island, Japan, then prepared polypropylene samples containing cuprous oxide and studied their accelerated marine degradation using sulfate ion radical initiation to clarify interactions between antifouling paint and microplastic breakdown.
Microplastics (MP) encompass not only plastic products but also paint particles. Marine microdebris, including MP, was retrieved from five sampling stations spanning Nagasaki-Goto island and was classified into six types, primarily consisting of MP (A), Si-based (B), and Cu-based (C) paint particles. Type-A particles, i.e., MP, were exceedingly small, with 74% of them having a long diameter of 25 µm or less. The vertical distribution of type C, containing cuprous oxide, exhibited no depth dependence, with its dominant size being less than 7 μm. It was considered that the presence of type C was associated with a natural phenomenon of MP loss. To clarify this, polypropylene (PP) samples containing cuprous oxide were prepared, and their accelerated degradation behavior was studied using a novel enhanced degradation method employing a sulfate ion radical as an initiator. Infrared spectroscopy revealed the formation of a copper soap compound in seawater. Scanning electron microscopy/energy-dispersive X-ray spectroscopy analysis indicated that the chemical reactions between Cl- and cuprous oxide produced Cu+ ions. The acceleration of degradation induced by the copper soap formed was studied through the changes in the number of PP chain scissions, revealing that the presence of type-C accelerated MP degradation.
More Papers Like This
Verification of the existence of copper-based antifouling paint particles in the sea and their implications for marine microplastic degradation
AI summary Read the abstract
Researchers collected marine debris near Nagasaki, Japan, and found copper-based antifouling paint particles alongside conventional microplastics at several sampling stations. These copper-based particles differ in chemical composition from typical plastic debris and may influence surrounding microplastic degradation patterns. The co-occurrence raises new questions about combined effects of paint particles and microplastics in marine environments.
Verification of the existence of copper-based antifouling paint particles in the sea and their implications for marine microplastic degradation
AI summary Read the abstract
Researchers collected marine debris samples near Nagasaki, Japan, and found that copper-based antifouling paint particles are widespread in the sea alongside conventional microplastics. The copper-based particles showed no depth-dependent distribution, unlike typical microplastics. Their presence may interact with or influence the degradation of surrounding plastic debris.
Co-occurrence of microplastics and microparticles containing Cu and Zn and other heavy metals in sea-surface microlayer in Osaka Bay, Japan
AI summary Read the abstract
Researchers analyzed tiny particles floating on the sea surface in Osaka Bay, Japan, and found microplastics containing heavy metals like copper and zinc from ship antifouling paints. Most of these metal-laden particles were made of acrylic resins commonly used in marine coatings, carrying copper concentrations up to 54,000 mg/kg. The study reveals that antifouling paint fragments are a significant and underrecognized source of toxic metal-containing microplastics in coastal waters.
Deterioration of marine antifouling coatings fragments and their possible environmental significance
AI summary Read the abstract
Ship hulls are coated with paint that prevents barnacles and algae from growing on them, but this paint breaks down into microplastic fragments that leach toxic metals like copper and zinc into the ocean. This new study found that sunlight and wave action speed up this breakdown significantly, meaning more of these contaminated plastic particles could be entering marine waters—and potentially the seafood we eat—than previously realized, especially in sunny, choppy coastal areas near busy ports.
Release of microplastics and metals from antifouling paint during weathering in simulated cold climates.
AI summary Read the abstract
Researchers subjected marine antifouling paint coatings to UV irradiation, freeze-thaw cycling, and their combination over 42 days, finding that both pathways release microplastics and metals into water — UV through oxidative polymer breakdown and freeze-thaw through ice abrasion — with the combined treatment releasing the highest concentrations of copper and zinc, and paint microplastics retaining chemical signatures traceable back to the source coating.