A Study of Plant-Filled Polymer Composites Based on Highly Plasticized Polyvinyl Chloride

To enhance the ecological properties of polyvinyl chloride (PVC) products, the fabrication of PVC-based composites using biofillers with acceptable performance characteristics could be considered. In this work, plant-filled PVC-based composite materials were fabricated and their optical, structural, thermal, and mechanical properties, depending on the nature of the filler, were studied. Spruce flour, birch flour, and rice husk were used as fillers. Optical measurements showed the selected technological parameters, allowing films with a uniform distribution of dispersed plant filler in the polymer matrix to be obtained. Using the plant fillers in PVC films leads to a reduction in strength characteristics; for instance, the tensile strength changed from 18.0 MPa (for pure PVC film) to ~7 MPa (for composites with 20 wt.% of fillers), and to ~5-6.2 MPa (for composites with 40 wt.% of fillers). Thermal investigations showed that the samples with plant fillers could be used at low temperatures without changing their operating characteristics. Thus, plant-filled PVC-based composite materials have a wide operating temperature range, from-65 °C to 150 °C. TGA analysis has demonstrated that the rice husk affected the thermal stability of the composites by increasing their thermal decomposition resistance. The ability to absorb water was observed during the investigation of water absorption of the samples. And the highest degree of water absorption (up to 160 mg/g) was detected for the sample with 40 wt.% of rice husk. In general, plant-filled polymer composites based on PVC can be used on an equal basis with unfilled PVC plastic compounds for some applications such as in construction (for example, for design tasks).