Abrasion Behaviors of Silica-Reinforced Solution Styrene–Butadiene Rubber Compounds Using Different Abrasion Testers

Solution styrene-butadiene rubber (SSBR) is widely used to improve the properties of tire tread compounds. Tire wear particles (TWPs), which are generated on real roads as vehicles traverse, represent one of significant sources of microplastics. In this study, four SSBR compounds were prepared using two SSBRs with high styrene (STY samples) and 1,2-unit (VIN samples) contents, along with dicyclopentadiene resin. The abrasion behaviors were investigated using four different abrasion testers: cut and chip (CC), Lambourn, DIN, and laboratory abrasion tester (LAT100). The abrasion rates observed in the Lambourn and LAT100 abrasion tests were consistent with each other, but the results of CC and DIN abrasion tests differed from them. The addition of the resin improved the abrasion rate and resulted in the generation of large wear particles. The abrasion rates of STY samples in the Lambourn and LAT100 abrasion tests were lower than those of VIN samples, whereas the values in the CC and DIN abrasion tests were higher than those of VIN samples. The wear particles were predominantly larger than 1000 μm, except for the VIN sample in the DIN abrasion test. However, TWPs > 1000 μm are rarely produced on real roads. The size distributions of wear particles > 1000 μm were 74.0-99.5%, 65.9-93.4%, 7.2-95.1%, and 37.5-83.0% in the CC, Lambourn, DIN, and LAT100 abrasion tests, respectively. The size distributions of wear particles in the Lambourn and LAT100 abrasion tests were broader than those in the other tests, whereas the distributions in the CC abrasion test were narrower. The abrasion patterns and the morphologies and size distributions of wear particles generated by the four abrasion tests varied significantly, attributable to differences in the bound rubber contents, crosslink densities, and tensile properties.