Photo-Induced Super-Hydrophilicity of Nano-Calcite @ Polyester Fabric: Enhanced Solar Photocatalytic Activity against Imidacloprid
Summary
Researchers grew nano-calcite crystals onto polyester fabric and found that brief UV irradiation transformed the surface from highly water-repellent to superhydrophilic while also narrowing the material's band gap, enabling the resulting photocatalyst to degrade 94% of the pesticide imidacloprid in wastewater over 10 reuse cycles using solar light.
[Image: see text] The present study is pertinent to photo-induced, hydrophilic, nano-calcite grown onto the mercerized surface of polyester fabric (PF), treated with UV (10–50 min) and visible light (1–5 h) in addition to its photocatalytic application. The wicking method has been employed to select the most hydrophilic sample of fabric upon irradiation. The micrographs obtained by scanning electron microscopy, transmission electron microscopy, and high-resolution transmission electron microscopy indicated the erosions occurring at the surface of nano-calcite after UV light irradiation, maintaining the crystallinity of the photocatalyst. The surface charge has been measured for as-fabricated and irradiated nano-calcite @ PF for the development of high negative zeta potential after UV light irradiation (−24.6 mV). The irradiated nano-calcite @ PF exhibited a significant change in its contact angle, and the wetting property was enhanced to a considerable extent on UV (55.32°) and visible light irradiation (79.00°) in comparison to as-fabricated nano-calcite @ PF (137.54°). The irradiated samples of nano-calcite @ PF delineated the redshift in harvesting of solar spectrum, as revealed by diffuse reflectance spectroscopy comparative spectra. Additionally, the band gap of untreated nano-calcite was found to be 3.5 eV, while UV- and visible light-irradiated PF showed a reduction in band gap up to 2.95 and 3.15 eV upon UV and visible light irradiation. The photocatalytic efficiency of mesoporous nano-calcite was evaluated by photocatalytic degradation of imidacloprid as the probe pollutant. Higher solar photocatalytic degradation of imidacloprid (94.15%) was attained by UV light-irradiated nano-calcite @ PF. The time-resolved photoluminescence study has verified the high photocatalytic activity of UV light-irradiated nano-calcite @ PF for the generation of high concentration of hydroxyl radicals. The highly efficient reusability of a nano-calcite-based solar photocatalytic reactor has been observed for 10 cycles of treatment of imidacloprid bearing wastewater. The enhanced photocatalytic activity of UV light-exposed (20 min), superhydrophilic, nano-calcite @ PF for mineralization of pollutants suggests it to be an efficient solar photocatalyst for environmental applications.